研究了少量NiO(0.25 mol%～1 mol%)添加剂对3Y-TZP陶瓷材料烧结和力学性能的影响.实验结果表明:掺杂NiO可以促进3Y-TZP的烧结,并提高材料的力学性能,但添加过量则对烧结和力学性能不利.经过1400 ℃,2 h烧成后,掺有0.5 mol%NiO的试样和掺有0.75 mol%NiO的试样分别具有最高的抗弯强度和断裂韧性,其值分别为419MPa和10.0 MPa·m1/2.与同样条件下制备出的纯3Y-TZP相比,试样的抗弯强度和断裂韧性分别提高了22%和47%.
参考文献
| [1] | Hodgson S N B;Cawley J;Clubley M .[J].Journal of Materials Processing Technology,1999,92-93:85. |
| [2] | 毛骏飙;陈楷;陈少贞 .[J].无机材料学报,1997,12(05):687. |
| [3] | LiI J F;Watanabe R .[J].Journal of Materials Science,1997,32:1149. |
| [4] | 靳喜海,丁湘,姜文博,陈玉如.五价钽、锂掺杂对Y-TZP微观结构和性能的影响[J].硅酸盐通报,1999(02):52-54. |
| [5] | Yang SY;Lee JH;Kim JJ;Lee JS .Sintering behavior of Y-doped ZrO2 ceramics: the effect of Al2O3 and Nb2O5 addition[J].Solid state ionics,2004(1/4):413-416. |
| [6] | Kuzjukevics A;Linderoth S .[J].Materials Science and Engineering A,1997,232:163. |
| [7] | Kuzjukevics A.;Linderoth S. .INTERACTION OF NIO WITH YTTRIA-STABILIZED ZIRCONIA[J].Solid state ionics,1997(3/4):255-261. |
| [8] | Kondo H;Sekino T;Kusunose T et al.[J].Journal of the American Ceramic Society,2002,86(03):523. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%