对TiAl3和Cr3C2金属间化合物复合材料的3种粉芯丝材CCW1、CCW2、CCW3进行N2保护和无N2保护的超音速电弧喷涂试验,结合金相、硬度、SEM、能谱分析对喷涂层的组织结构及其高温冲蚀性能进行试验研究.结果表明,氧化夹杂物明显降低凝片与凝片之间的结合状况,冲蚀磨损导致凝片与凝片分离、凝片断裂、掀起和剥落;N2保护下的电弧喷涂层比无保护时的涂层更为致密和均匀,氧化夹杂物明显减少,硬度显著提高.试验条件下,N2保护的3种粉芯丝材电弧喷涂层平均体积冲蚀率分别降低了3.3、2.3和1.0倍.
参考文献
| [1] | Liu Shaoguang;Wu Jinming;Zhang Shengcai et al.[J].Wear,2007,262:555-561. |
| [2] | Sampath S;Jiang X Y et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,364(1-2):216-231. |
| [3] | 刘少光,吴进明,张升才,胡小海,荣淑杰,李志章.超临界锅炉管道耐磨涂层的微观组织结构及冲蚀规律[J].动力工程,2006(06):908-912. |
| [4] | Wu J M;Zheng S L;Li Z Z .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2000,289(1-2):246-254. |
| [5] | Wang BQ.;Seitz MW. .Comparison in erosion behavior of iron-base coatings sprayed by three different arc-spray processes[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(1):755-761. |
| [6] | 刘少光,吴进明,张升才,荣淑杰,胡小海,李志章.退火处理对含纳米陶瓷粉电弧喷涂层组织结构与高温冲蚀性能的影响[J].功能材料,2006(12):2023-2026. |
| [7] | Wang B Q .[J].Wear,1999,225-229(01):502-509. |
| [8] | Stringer J .[J].Wear,1995,186-187:11-27. |
| [9] | 刘少光;吴进明;张升才.[J].浙江大学学报(工学版),2007 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%