采用溶胶-凝胶(Sol-Gel)浸渍提拉法在AZ91D镁合金表面制备不同pH值下的SiO2溶胶-凝胶膜层；对膜层耐酸性、耐碱性、抗氧化性及耐蚀性等性能进行测试和表面形貌分析.结果表明,当SiO2溶胶组分比(正硅酸乙酯:无水乙醇:蒸馏水的物质的量之比)为1:15:9.5,浸渍时间为120 s,浸渍次数为1,干燥温度为120℃时,调节溶胶的pH值为2.8,可获得均匀、重复性好的SiO2溶胶凝胶膜,该膜层具有良好的耐蚀性.
参考文献
| [1] | 张晨曦,邵红红,刘贵维.提高AZ91D镁合金表面耐腐蚀性能的研究[J].轻金属,2008(10):55-57. |
| [2] | Chong KZ.;Shih TS. .Conversion-coating treatment for magnesium alloys by a permanganate-phosphate solution[J].Materials Chemistry and Physics,2003(1):191-200. |
| [3] | Yfantis A.;Paloumpa I.;Schmeisser D.;Yfantis D. .Novel corrosion-resistant films for Mg alloys[J].Surface & Coatings Technology,2002(0):400-404. |
| [4] | Umehara H.;Takaya M.;Terauchi S. .Chrome-free surface treatments for magnesium alloy[J].Surface & Coatings Technology,2003(0):666-669. |
| [5] | Phani AR;Gammel FJ;Hack T .Structural, mechanical and corrosion resistance properties of Al2O3-CeO2 nanocomposites in silica matrix on Mg alloys by a sol-gel dip coating technique[J].Surface & Coatings Technology,2006(6):3299-3306. |
| [6] | 许越,李英杰,吕祖舜,郭愿东,杨昱.Sol-gel法制备耐蚀涂层的技术及应用[J].材料科学与工艺,2005(02):200-204. |
| [7] | 王秀华,孙益民,刘守华,孙红霞,沈业青.有机-无机杂化涂层制备及耐腐蚀性能研究[J].腐蚀科学与防护技术,2006(04):292-294. |
| [8] | 蒋奎胜,唐聿明,赵旭辉,左禹.电流密度对AZ91D镁合金阳极氧化膜表面形貌及粘接性能的影响[J].材料研究学报,2010(03):305-310. |
| [9] | 时海芳,李晓,马壮,李智超.MB2镁合金SiO2基陶瓷涂层的性能[J].腐蚀与防护,2008(08):457-459. |
| [10] | 郭志光,周峰,刘维民.溶胶凝胶法制备仿生超疏水性薄膜[J].化学学报,2006(08):761-766. |
| [11] | 罗小萍,夏兰廷,臧东勉.镁合金表面化学转化处理研究现状[J].铸造设备研究,2007(02):44-47. |
| [12] | 张军军,李文芳,杜军.室温下铝合金表面Ce-Mn转化膜的制备及性能[J].金属学报,2009(12):1466-1472. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%