采用沉淀法合成了粒径为40～50nm的硼酸镍纳米微粒,利用透射电镜、X射线粉末衍射仪、热分析仪、FT-IR光谱仪等进行了结构表征,利用四球摩擦试验机考察了其在水溶液中的摩擦学行为,并利用电子扫描电镜考察了磨损表面的形貌.结果表明:硼酸镍纳米微粒作为水基添加剂能显著提高水的抗磨减摩性能,作用机理是发生了摩擦化学反应,在摩擦副表面生成了含Ni2O3、FeO、Fe0和Fe2O3的复合润滑膜,所以能有效提高水的抗磨减摩性能.
参考文献
| [1] | Morikawa A;Lyoku Y et al.Preparation of a new class of polyimide-silica hybrid films by sol-gel process[J].Polymer Journal,1992,24(01):107. |
| [2] | Chen Shuang;Liu Weimin .Synthesis and investigation of DDP-capped PbS nanoparticles as an antiwear additive[J].Tribology,1997,17(13):260. |
| [3] | Zhang Zhijun;Zhang Ju et al.Synthesis and characterization of a molybdenum disulfide nanocluster[J].Physical Chemistry,1994,98:12973. |
| [4] | Zhang Zhijun;Xue Qunji et al.Synthesis,structure and lubricating properties of dialkyldithiophosphare-modified MoS compounds nanocluster[J].Wear,1997,209:8. |
| [5] | 高永建,张治军,薛群基,党鸿辛.油酸修饰TiO2纳米微粒水溶液润滑下GCr15钢摩擦磨损性能研究[J].摩擦学学报,2000(01):22-25. |
| [6] | 孙蓉,李明静,高永建,张治军,党鸿辛.TiO2纳米微粒-茶皂素水基乳化液的切削行为研究[J].摩擦学学报,2002(04):254-257. |
| [7] | 薛群基;刘维民;李斌 等.水基润滑的纳米金属减磨抗摩强化剂[P].CN 1552833A,2004-12-08. |
| [8] | 李强,郝春成.表面修饰纳米硼酸锌粒子的制备与摩擦学性能研究[J].青岛科技大学学报（自然科学版）,2006(01):44-46,49. |
| [9] | 荆煦瑛.红外光谱使用指南[M].天津:天津科学技术出版社,1992 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%