从氧化动力学、氧化膜相组成及微观结构方面,研究了晶粒尺寸对18Cr-8Ni耐热钢在700℃下的高温水蒸汽中氧化行为的影响.结果表明:晶粒细化提高了耐热钢的抗水蒸汽氧化性能,降低了其氧化增重,推迟了失稳氧化的发生；晶粒细化改变了耐热钢氧化膜的微观结构,减小了“弹坑”区的尺寸且促进了“弹坑”区与合金界面上富Cr氧化物层的形成；晶粒细化对耐热钢抗水蒸汽氧化性能的改善主要归因于其对氧化物的形核和Cr向氧化膜/合金界面扩散的促进作用.
参考文献
| [1] | I. G. Wright;R. B. Dooley .A review of the oxidation behaviour of structural alloys in steam[J].International Materials Reviews,2010(3):129-167. |
| [2] | H. Asteman;J.-E. Svensson;L.-G. Johansson .Evidence for Chromium Evaporation Influencing the Oxidation of 304L: The Effect of Temperature and Flow Rate[J].Oxidation of Metals,2002(3/4):193-216. |
| [3] | D. J. Young;B. A. Pint .Chromium Volatilization Rates from Cr_2O_3 Scales into Flowing Gases Containing Water Vapor[J].Oxidation of Metals,2006(3/4):137-153. |
| [4] | A. N. Hansson;H. Danielsen;F. B. Grumsen;M. Montgomery .Microstructural investigation of the oxide formed on TP 347H FG during long-term steam oxidation[J].Materials and Corrosion,2010(8):665-675. |
| [5] | J. Jianmin;M. Montgomery;O. H. Larsen;S. A. Jensen .Investigation on steam oxidation behaviour of TP347H FG - Part 1: Exposure at 256 bar[J].Materials and Corrosion,2005(7):459-467. |
| [6] | J. Jianmin;M. Montgomery;O. H. Larsen;S. A. Jensen .Investigation of steam oxidation behaviour of TP347H FG - Part 2: Exposure at 91 bar[J].Materials and Corrosion,2005(8):542-549. |
| [7] | 李辛庚,何家文.喷丸处理提高TP304H耐热钢锅炉管抗水蒸气氧化性能应用效果的观察[J].中国腐蚀与防护学报,2003(03):171-174. |
| [8] | L. Sanchez;M. P. Hierro;F. J. Perez .Effect of Chromium Content on the Oxidation Behaviour of Ferritic Steels for Applications in Steam Atmospheres at High Temperatures[J].Oxidation of Metals,2009(3/4):173-186. |
| [9] | Dionisio Laverde;Tomas Gomez-Acebo;Francisco Castro .Continuous and cyclic oxidation of T91 ferritic steel under steam[J].Corrosion Science,2004(3):613-631. |
| [10] | R. Naraparaju;V. B. Trindade;H.-J. Christ;U. Krupp .Effect of shot peening on high temperature oxidation behaviour of boiler steel: experimental results and simulation[J].Corrosion Engineering, Science and Technology,2009(3):211-217. |
| [11] | R. Naraparaju;H.-J. Christ;F. U. Renner .Effect of Shot-peening on the Oxidation Behaviour of Boiler Steels[J].Oxidation of Metals,2011(3/4):233-245. |
| [12] | Yue Zengwu;Fu Min;Wang Xuegang .Effect of Shot Peening on the Oxidation Resistance of TP304H and HR3C Steels in Water Vapor[J].Oxidation of Metals,2012(1/2):17-26. |
| [13] | 岳增武,傅敏,李辛庚,田学雷.内壁喷丸处理对TP304H耐热钢锅炉管抗水蒸汽氧化性能的影响[J].中国腐蚀与防护学报,2012(02):137-140. |
| [14] | X. Peng;J. Yan;Y. Zhou .Effect of grain refinement on the resistance of 304 stainless steel to breakaway oxidation in wet air[J].Acta materialia,2005(19):5079-5088. |
| [15] | A. N. Hansson;K. Pantleon;F. B. Grumsen .Microstructure Evolution During Steam Oxidation of a Nb Stabilized Austenitic Stainless Steel[J].Oxidation of Metals,2010(1/2):289-309. |
| [16] | Z. Huang;X. Peng;C. Xu .Effect of Alloy Nanocrystallization and Cr Distribution on the Development of a Chromia Scale[J].Journal of the Electrochemical Society,2009(3):C95-C102. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%