The glass formation was investigated in the melt-spun Al-rich AI-Co-Y alloys by the microstructure evolution.The best glass former Al88Co5Y7 with the thickness of 230 μm was found, and its glass forming ability (GFA) was higher than that of previously reported Al88Co4Y8 alloy. This result indicates that GFA is strongly sensitive to the alloy composition in the system. The phase selection method is an effective way to locate the optimum glass formation composition rather than Trg and △Tx parameters.
参考文献
| [1] | A.Inoue .Stabilization of metallic supercooled liquid and bulk amorphous alloys[J].Acta materialia,2000(1):279-306. |
| [2] | W L Johnson .[J].MRS Bulletin,1999,24:42. |
| [3] | W.H. Wang;C. Dong;C.H. Shek .Bulk metallic glasses[J].Materials Science & Engineering, R. Reports: A Review Journal,2004(2/3):45-89. |
| [4] | A Inoue;T Zhang;T Masumoto .[J].Materials Transactions-Japan Institute of Metals,1989,30:956. |
| [5] | Z P Lu;C T liu;J R Thompson;W D Porter .[J].Physical Review Letters,2004,92:245503. |
| [6] | D H Xu;G Duan;W L Johnson .[J].Physical Review Letters,2004,92:245504. |
| [7] | H Ma;L L Shi;J Xu;Y Li and E Ma .[J].Journal of Materials Research,2006,21(09):2204. |
| [8] | Y He;S J Poon;G J Shiflet .[J].Science,1988,241:241. |
| [9] | A Inoue .[J].Progress in Materials Science,1998,43:365. |
| [10] | W. S. Sanders;J. S. Warner;D. B. Miracle .Stability of Al-rich glasses in the Al-La-Ni system[J].Intermetallics,2006(3):348-351. |
| [11] | H. Tan;Y. Zhang;D. Ma .Optimum glass formation at off-eutectic composition and its relation to skewed eutectic coupled zone in the La based La-Al-(Cu, Ni) pseudo ternary system[J].Acta materialia,2003(15):4551-4561. |
| [12] | D Wang;H Tan;Y Li;E Ma .[J].Applied Physics Letters,2005,86:191906. |
| [13] | X Hu;S C Ng;Y P Feng;Y Li .[J].Acta Materials,2003,51:56. |
| [14] | D Ma;Y A Chang .[J].Acta Materials,2006,54:1927. |
| [15] | D Wang;Y Li;B B Sun;M L Sui K Lu and E Ma .[J].Applied Physics Letters,2004,84:4029. |
| [16] | Y. Zhang;W. Xu;H. Tan .Microstructure control and ductility improvement of La-Al-(Cu, Ni) composites by Bridgman solidification[J].Acta materialia,2005(9):2607-2616. |
| [17] | H Yang;J Q Wang;Y Li .[J].Philosophical Magazine,2007,87:4211. |
| [18] | A L Greer .[J].Nature,1993,366:303. |
| [19] | A Inoue;N Matsumoto;T Masumoto .[J].Materials Transactions-Japan Institute of Metals,1990,31:493. |
| [20] | Y He;G J Shiflet;S J Poon .[J].Journal of Alloys and Compounds,1994,207:340. |
| [21] | H W Yang;P Dong;J Q Wang;Y Li .[J].Materials Science and Engineering A,449-451:273. |
| [22] | P Villars;A Prince;H Okamoto.Handbook of Ternary Alloy Phase Diagrams[M].ASM International,Materials Park,OH,1997:3092. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%