采用冷冻干燥/粒子沥滤复合法制备聚己内酯(PCL)多孔支架,通过扫描电镜对支架的三维结构进行了表征,并计算了支架孔隙率.研究结果表明,与单一冷冻干燥法或粒子沥滤法相比,复合法制备的PCL支架具有孔隙率高(86%),孔隙结构均匀、孔隙连通性好、孔径可控等特点,支架结构可以通过调整预冷冻温度和造孔剂粒径进行控制.
参考文献
[1] | 陆蓉,李世普,闫玉华.组织工程用聚合物多孔支架的制备技术[J].生物骨科材料与临床研究,2005(03):37-41. |
[2] | 於秋霞,朱光明,梁国正,杜宗刚,宫兆合.聚ε-己内酯的合成、性能及应用进展[J].高分子材料科学与工程,2004(05):37-40,45. |
[3] | 艾合麦提·玉素甫,王振斌,朱良.可生物降解材料聚己内酯在医学上的应用进展[J].国外医学(生物医学工程分册),2005(01):19-23. |
[4] | Wu L;Ding J .In vitro degradation of three-dimensional porous poly(d,l-lactide-co-glycolide) scaffolds for tissue engineering.[J].Biomaterials,2004(27):5821-5830. |
[5] | 吴林波,丁建东.组织工程三维多孔支架的制备方法和技术进展[J].功能高分子学报,2003(01):91-96. |
[6] | Nam YS;Park TG .Porous biodegradable polymeric scaffolds prepared by thermally induced phase separation.[J].Journal of biomedical materials research, Part B. Applied biomaterials,1999(1):8-17. |
[7] | Harris LD;Kim BS;Mooney DJ .Open pore biodegradable matrices formed with gas foaming.[J].Journal of biomedical materials research, Part B. Applied biomaterials,1998(3):396-402. |
[8] | Wu LB;Jing DY;Ding JD .A "room-temperature" injection molding/particulate leaching approach for fabrication of biodegradable three-dimensional porous scaffolds[J].Biomaterials,2006(2):185-191. |
[9] | Yang K F;Leong Z D;Chua C K .The design of scaffolds for use in tissue engineering:Part Ⅱ.Rapid prototyping techniques[J].Tissue Engineering,2002,8(01):1. |
[10] | 刘斌,郭超,董寅生,林萍华.组织工程用多孔支架制备工艺进展[J].武汉化工学院学报,2003(03):66-71. |
[11] | 刘培生.多孔材料引论[M].北京:清华大学出版社,2004:300. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%