利用Ni与CeO2纳米颗粒共电沉积在A3钢表面制备了一层纳米晶结构的Ni-CeO2复合膜（镍晶粒平均尺寸为60±38 nm），然后在600℃扩散渗铝5小时获得一种新型CeO2改性的低温渗铝涂层.同时,在上述条件下制备了单镀镍渗铝涂层以及A3钢渗铝涂层作为对比.550℃~850℃模拟流化床燃煤环境中100 h冲蚀/腐蚀实验表明，Ni-CeO2复合膜渗铝涂层较单镀镍渗铝涂层和A3钢渗铝涂层具有更好的抗冲蚀/腐蚀能力.
参考文献
| [1] | MA Uusitalo,P M J Vuoristo,T A Mantyla.Elevated tempera-ture erosion-corrosion of thermal sprayed coatings in chlorinecontaining environments[J].Wear,2002,252:586. |
| [2] | L Huilin,Z Guangbo,B Rushan,et al.A coal combustion modelfor circulating fluidized bend boiler[J].Fuel,2000,79:165. |
| [3] | R Viswanathan,J F Henry,J Tanzosh,et al.US Program on ma-terials technology for ultra-supercritical coal power plants[J].Adv.Mater.Proc.,2005,14:281. |
| [4] | Ruth LA.Advanced clean coal technology in the US A[J].Ma-ter.High Temp.,2003,20:7. |
| [5] | X Peng,K Liu,W P Pan,et al.High-temperature Corrosion ofA210-C Carbon steel in simulated coal-combustion atmospheres[J].Oxid.Met.2003,60:117. |
| [6] | K Segerdahl,J-E Svensson,L G.Johansson.Protective and non-protective behavior of 11%Cr steel in O2+H2O environment[J].J.Electrochem.Soc.,2004,151:B394. |
| [7] | HS Hsu.Reviewof the development and breakdown of protectiveoxide scales on alloys exposed to coal-derived atmospheres[J].Oxid.Met.,1987,28:213. |
| [8] | K Natesan.Application of coatings in coal-fired energy system[J].Surf.Coat.Technol.,1993,56:185. |
| [9] | L Zhu,X Peng,J Yan,et al.Oxidation of a novel chromium coat-ing with CeO2dispersions[J].Oxid.Met.,2004,62:411. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%