几何尺寸和物性参数对铝硅闭孔泡沫材料动态力学性能影响较大.消除材料自身尺寸效应的影响,采用落锤冲击实验方法对不同几何尺寸和物性参数的泡沫材料进行冲击实验,研究几何尺寸和物性参数对材料冲击吸能特性的影响.冲击实验结果表明:(1)材料几何高度增加,冲击作用下应变值减小,吸能量却有减小趋势,说明材料几何高度增大,极易产生材料孔壁破裂或整体失稳破坏,造成材料抵抗冲击载荷能力降低,立方体试件高宽比在1.0～1.5之间为宜,圆柱体试件高宽比为1.0～2.0时缓冲吸能作用发挥较好；(2)随着材料直径增大,抗压强度值增加,且峰值后降低幅值减小,应变值逐渐减小,说明材料直径的增加提高了抗压强度值,增强了材料抗冲击能力,但直径增加有一定界限,圆柱和立方体高宽比为1.0左右为宜；(3)材料密度越大,抗压强度值也越高,但峰值后的突降也越大；材料乳隙度越大,抗压强度值越小,材料易产生破坏,抗冲击能力也较低；材料孔径增大,抗压强度值降低,但变形量增加,受冲击载荷作用影响较大;(4)对比结果得到冲击吸能效果良好的泡沫材料合理物性参数,密度为0.35～0.70g/cm3,孔隙度为65％～87％,孔径为1.0～4.0mm.
参考文献
| [1] | 陈利;刘春雷;张庆明 et al.闭孔泡沫镁材料静动态压缩力学性能与吸能特性[J].兵工学报,2009,30(增刊2):197. |
| [2] | Gibson L J;Ashby M F.Cellular solids:Structure and properties[M].Oxford:pergamon Press,1997:113. |
| [3] | Banhart J .Manufacture,characterization and application of cellular metals and metal foams[J].Progress in Materials Science,2001,46:559. |
| [4] | McCullough K Y G;Fleck N A;Ashby M A .Uniaxial stress-strain behaviour of aluminum alloy foams[J].Acta Materialia,1999,47(08):2323. |
| [5] | 卢子兴,郭宇.金属泡沫材料力学行为的研究概述[J].北京航空航天大学学报,2003(11):978-983. |
| [6] | 郭刘伟,虞吉林.泡沫铝夹芯双方管结构准静态轴压性能的实验研究[J].实验力学,2010(03):271-278. |
| [7] | 刘耀东,虞吉林,郑志军.惯性对多孔金属材料动态力学行为的影响[J].高压物理学报,2008(02):118-124. |
| [8] | 寇东鹏,虞吉林,郑志军.随机缺陷对蜂窝结构动态行为影响的有限元分析[J].力学学报,2009(06):859-868. |
| [9] | 张健,赵桂平,卢天健.闭孔泡沫铝应变率效应的试验和有限元分析[J].西安交通大学学报,2010(05):97-101. |
| [10] | P.J. Tan;S.R. Reid;J.J. Harrigan;Z. Zou;S. Li .Dynamic compressive strength properties of aluminium foams. Part Ⅰ—experimental data and observations[J].Journal of the Mechanics and Physics of Solids,2005(10):2174-2205. |
| [11] | Jeon I;Asahina T .The effect of structural defects on the compressive behavior of closed-cell Al foam[J].Acta materialia,2005(12):3415-3423. |
| [12] | Chen Xiang;Li Yanxiang .Porous metals research advances and application[J].Materials Review,2003,17(05):5. |
| [13] | Kanahashi H;Mukai T;Yamada Y et al.Dynamic compression of an ultra-low density aluminum foam[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2000,280:349. |
| [14] | Wang Zhihua;Ma Hongwei;Zhao Longmao .Studies on the dynamic compressive properties of open-cell aluminum alloy foams[J].Scripta materialia,2006(1):83-87. |
| [15] | 索涛,邓琼,苗应刚,叶婷.基于Hopkinson压杆实验技术的含能材料动态力学性能测试方法研究进展[J].火炸药学报,2010(02):5-9. |
| [16] | 杨益,李晓军,郭彦朋.夹芯材料发展及防护结构应用综述[J].兵器材料科学与工程,2010(04):91-96. |
| [17] | 王礼立,杨黎明,周风华.强动载荷下结构的柔性防护和刚性防护[J].爆炸与冲击,2009(04):337-344. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%