试验研究了低碳钢变形后经历等温及随后快冷的组织转变,发现在Ae3附近及以下一定温度范围内大变形会使室温组织中出现超平衡数量的铁素体.形变后等温,出现超平衡数量铁素体向奥氏体的逆相变,该弛豫过程具有类似C曲线的动力学特征;而且经过等温后,伴随着铁素体数量的减少存在其晶粒尺寸增大的现象.随着变形温度的降低,超平衡数量铁素体在数量以及晶粒尺寸上的稳定性均提高.
参考文献
| [1] | Hiroshi YADA;Chun-Ming Li;Hiroshi YAMAGATA .Dynamic γ→α Transformation during Hot Deformation in Iron-Nickel-Carbon Alloys[J].ISIJ International,2000(2):200-206. |
| [2] | 杨平,傅云义,崔凤娥,孙祖庆.Q235碳素钢应变强化相变的基本特点及影响因素[J].金属学报,2001(06):592-600. |
| [3] | 杨忠民,赵燕,王瑞珍,马燕文,车彦民.形变诱导铁素体的形成机制[J].金属学报,2000(08):818-822. |
| [4] | Mintz B;Lewis J;Jonas JJ .Importance of deformation induced ferrite and factors which control its formation[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1997(5):379-388. |
| [5] | CHEN Ying;CHEN Qi-an .Dilator Investigation on Isothermal Transformation After Hot Deformation[J].Journal of Iron and Steel Research,2003,10(04):38-41. |
| [6] | Cahn J W .The Kinetics of Grain Boundary Nucleation Reactions[J].Acta Metalluraica,1956,4(09):449-459. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%