研究了加料工艺、引发剂体系、乳化剂用量及复配比、聚合温度等因素对多层核壳结构乳胶粒子粒径的影响,采用连续滴加单体的加料工艺,选用复配乳化剂体系,在较低的乳化剂用量条件下,使用高效低温引发剂,在50℃引发聚合,合成了固含量为42％,平均粒径为64.9 nm,窄分布的具有多层核壳结构的聚丙烯酸酯乳液.
参考文献
| [1] | ABIGAIL S KIMERLING;SURITA RBHATIA .Block copolymer as low VOC coatings for wood:characterization and tannin bleed resistance[J].Progress in organic Coatings,2004,51(01):15-26. |
| [2] | Carretti E;Giorgi R;Berti D;Baglioni P .Oil-in-water nanocontainers as low environmental impact cleaning tools for works of art: Two case studies[J].Langmuir: The ACS Journal of Surfaces and Colloids,2007(11):6396-6403. |
| [3] | Chevalier Y.;Cavaille J.-Y.;Cabane B.;Hidalgo M. .Structure of waterborne organic composite coatings[J].Macromolecules,1999(23):7887-7896. |
| [4] | 李秀艳,王平.乳液的最低成膜温度及其影响因素[J].涂料工业,2001(03):1-3. |
| [5] | 孙玉,郑帼,窦春花.烷基磷酸酯钾盐乳液粒径的研究[J].精细石油化工,2006(01):43-46. |
| [6] | 唐植贤,王君瑞,郑修斌.丙烯酸酯乳胶膜透明度和光泽度的影响因素探讨[J].上海涂料,2013(01):53-56. |
| [7] | VIJAY RAJAGOPALAN;ULF OLSSON;ILIAS ILIOPOULOS .Effect of absorbing polyelectrolytes on a balanced nonionie surfactant-water-oil system[J].LANGMUIR,1996,12(08):4378-4384. |
| [8] | 耿耀宗;曹同玉.合成聚合物乳液制造与应用技术[M].北京:中国轻工业出版社,1999:82-86. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%