在酸性环境下用化学氧化法合成了聚苯胺;制备了不同含量的本征态和掺杂态聚苯胺涂覆的碳钢试样,利用塔菲尔曲线比较了它们在质量分数为3.5%的NaCl和1 mol/L HCl溶液中的腐蚀行为.结果表明:当间甲酚固化剂作为溶剂、磷酸作为催化剂时,本征态聚苯胺涂层具有良好的防腐蚀性能;不同状态聚苯胺的防腐蚀性能与腐蚀介质有关,与聚苯胺的含量有关.