采用逐次回归方法对反应烧结制备的刚玉β-Sialon复合材料进行了分析. 研究了材料的体积密度、显气孔率及常温抗折强度与原料的颗粒配比之间的关系, 得到
了回归效果良好的数学模型, 验证结果表明回归方程的预报与实验值相当接近, 回归方程可用于刚玉/β-Sialon复合材料常温物理性能的预报.
In the investigations on sintering properties of corundum/β-Sialon composite materials prepared by reaction sintering, the stepwise regress method was used to establish the models of
properties (bulk density, apparent porosity, and modulus of rupture at room temperature). The results of checking experiments are in accordance with the regress values. This means that the models can
be used to forecast the sintering properties of corundum/β-Sialon composite.
参考文献
| [1] | Zheng Jie, Bertil Forslund. Journal of the European Ceramic Society, 1999, 19 (2): 175-185. [2] Gilbert J E, Mosset A. Materials Research Bulletin, 1998, 33 (1): 117-123. [3] Kudyba-Jansen A A, Hintzen J T, Metselaar R. Materials Research Bulletin, 2001, 36 (7): 1215-1230. [4] 张立明, 禄向阳. 耐火材料, 2001, 35 (1): 11-13. [5] 周丽红, 王鸿妹. 耐火材料, 2001, 35 (3): 161-162. [6] 都兴红, 张广荣, 张伟民等. 耐火材料, 1997, 31 (5): 275-278. [7] 罗积玉, 邢瑛. 经济统计分析方法及预测. 第一版. 北京: 清华大学出版社, 1987. 46-54. [8] 朱伟勇, 胡晨江. 最优设计的计算机证明与构造. 第一版. 沈阳: 东北工学院出版社, 1987. 383-472. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%