A reasonable pre-treatment and an ultrasonic pre-plating Cu film were applied for sintering NdFeB permanent magnet. The samples were then plated in neutral bath (PH=7) for 40min and in acidic bath (PH=4.8～5.1) for 2h. A composite electroless plating with different phosphor content was obtained. The results show that the composite plating coatings are dense and have a strong bond with the substrate, which contribute to the excellent corrosion resistance of the plating coating.
参考文献
| [1] | Lin Hecheng .The product and application of NdFeB permanent magnet in China[J].Nonferrous Metallurgy,2000,29:7-10. |
| [2] | He Yijun;Li Wei .The development of protection of NdFeB[J].Metallic Functional Materials(in Chinese)(金属功能材料),2002,8:8-12. |
| [3] | Wang Ruixiang .Electro-plating on the substrate of NdFeB[J].Electroplating and finishing,2000,19(05):18-20. |
| [4] | Ding guifu;Yao Jingyuan;Yang Chunsheng etc.Studies on the corrosion resistance of electroless Ni plating on NdFeB permanent magnet[J].Materials Protection,1997,30(03):6-8. |
| [5] | 郑华均,郑国渠,马淳安.化学镀镍磷合金工艺研究及其在钕铁硼永磁体抗蚀上的应用[J].表面技术,2002(02):42-45. |
| [6] | 于升学,宋伟明,邵光杰.烧结Nd-Fe-B永磁体化学镀Ni-Cu-P性能研究[J].热加工工艺,2001(04):41-42. |
| [7] | Hong Dong;Per M .Effects of pretreatment on the structure and properties of electroless nickel coatings[J].Plating and Surface Finishing,1994,81:73-77. |
| [8] | Tang Chunhua .The choose and application of Ni electroless plating[J].腐蚀与防护,2001,22(07):297-301. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%