利用JSM6700F冷场发射扫描电镜及其自带的能谱仪等分别对采用镍、镍+铜两种中间层的TC4/ZQSn10-10异种材料扩散连接接头进行了微观分析.结果表明:镍中间层能有效地阻止元素钛与铜之间的扩散,避免产生金属间化合物(Cu3Ti、CuTi等);但在TC4/Ni界面上仍有金属间化合物NiTi、Ni3Ti生成,使接头的抗拉强度有所降低;在适当压力和保温时间、镍为中间层时,较佳连接温度为830℃;镍+铜为中间层时,较佳连接温度为850℃;两者所得接头强度(155.8MPa)相当,均为ZQSn10-10母材强度的65%.
参考文献
| [1] | M.D. Chapetti .Application of a threshold curve model to high-cycle fatigue behavior of small cracks induced by foreign-object damage in Ti-6Al-4V[J].International Journal of Fatigue,2005(5):493-501. |
| [2] | Juan Wang;Yajiang Li;Peng Liu .XRD and TEM analysis on the Fe_3Al/18-8 stainless steel diffusion bonded interface[J].Materials Letters,2003(26/27):4323-4327. |
| [3] | Guo Wei,Zhao Xihua,Song Minxia,Feng Jicai,Yang Biao.Diffusion bonded transition joint of TC4 to QAl10-3-1.5[J].中国焊接,2005(02):109-112. |
| [4] | Tzanko Dimitrov Uzunov;Stojan Petrov Stojanov;Sashko Ivanov Lambov .Thin films of intermetallic Cu/Ti compounds and their possible uses[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,1999(3):321-325. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%