利用不同的锂化合物Li2CO3、LiOH.H2O、LiNO3、LiF作为锂源,采用二步固相法合成了LiFePO4/C,研究了不同锂源对LiFePO4组织结构和电化学性能的影响。结果表明,在相同的合成工艺条件下,采用4种不同锂源合成的LiFePO4的电化学性能表现出明显差异。采用LiOH.H2O合成的LiFe-PO4的电化学性能最佳,0.1C下的放电比容量为161mAh/g,1C下的放电比容量达117mAh/g,且0.5C下循环容量无衰减。采用不同锂源合成的LiFePO4电化学性能差异的原因与LiFePO4的颗粒大小、粒径分布、团聚程度及是否存在杂相有直接关系。
LiFePO4/C composites were synthesized by two step solid reaction process using Li2CO3,LiOH·H2O,LiNO3,LiF as Lisources.It was found that LiFePO4/C composites prepared with different Li-containing compounds exhibited obvious differences in the microstructure and electrochemical performance.LiFePO4/C synthesized by LiOH·H2O showed the best electrochemical property,with a high discharge capacity of 161mAh/g at 0.1C,117mAh/g at 1C and excellent cycle stability.The different electrochemical performances of LiFePO4/C composites by different Lisources may be contributed to their difference in the particle size,particle size distribution,degree of agglomeration and purity.
参考文献
| [1] | 刘会平,王志兴,李新海,郭华军,彭文杰.用碳热还原法制备LiFePO4/C复合正极材料[J].功能材料,2008(08):1302-1305. |
| [2] | 张欣,唐致远,滕国鹏,李中延.锂离子电池LiFePO4新型合成方法及改性研究[J].材料导报,2008(z1):255-257. |
| [3] | Sanchez MAE;Brito GES;Fantini MCA;Goya GF;Matos JR .Synthesis and characterization of LiFePO4 prepared by sol-gel technique[J].Solid state ionics,2006(5/6):497-500. |
| [4] | 王素敏,黄学杰,薛荣坚,陈立泉.高性能LiNiO2制备方法的研究[J].稀有金属,1999(05):353-356. |
| [5] | 阮艳莉,唐致远.LiFePO4的合成及其热分析动力学[J].物理化学学报,2008(05):873-879. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%