采用机械合金化结合真空烧结法制备了掺钴的N型β-FeSi2热电材料Fe0.95Co0.05Si2,利用XRD和SEM分析了该材料的物相组成和显微形貌,对机械合金化粉体进行了DSC分析,并对烧结试样进行了热电性能测试.结果表明:球磨5 h后铁、钴、硅混合物可完全合金化,全部生成β-FeSi2、α-Fe2Si5和ε-FeSi相;随着球磨时间延长,合金粉体更加均匀细小,β-FeSi2的含量逐渐增加;机械合金化20 h的粉体压制后经过1 373 K烧结2 h和1 073 K烧结2 h,可获得单相β-FeSi2材料;合金粉体在1 177 K开始分解;随着温度升高,Fe0.95Co0.05Si2试样的Seebeck系数α、电导率σ增大,热导率K降低,而无量纲热电优值明显增大,在773 K时最大,为0.11.
参考文献
| [1] | E. BELYAEV;S. MAMYLOV;O. LOMOVSKY .Mechanochemical synthesis and properties of thermoelectric material β-FeSi_(2)[J].Journal of Materials Science,2000(8):2029-2035. |
| [2] | Mikio Ito;Hiroshi Nagai;Shigeru Katsuyama .Effects of Ti, Nd and Zr doping on thermoelectric performance of #beta#-FeSi_2[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2001(1/2):251-258. |
| [3] | Sridhar K.;Chattopadhyay K. .Synthesis by mechanical alloying and thermoelectric properties of Cu2Te[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,1998(1/2):293-298. |
| [4] | 周芸,周兆,沈容.机械合金化制备β-FeSi2热电材料的研究[J].粉末冶金技术,2004(04):228-231. |
| [5] | 李红星,赵新兵,李伟文.新型热电材料研究进展[J].材料导报,2002(06):20-23. |
| [6] | 李凡,吴炳尧,戴挺,吴正华,王有明.机械合金化法制备Fe-Si纳米晶合金[J].特种铸造及有色合金,2001(04):24-26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%