煤焦油沥青在微型高压釜中、氮气氛下,通过改变反应温度和停留时间,制取了中间相沥青(MP).采用FTIR、偏光显微镜、XRD和SEM对MP进行了表征,表明煤焦油沥青经脱氢缩合反应转变成MP.其最佳反应条件为400℃、7h.
Mesophase pitch (MP) was produced by heating coal tar pitch in a microautoclave furnace at various temperatures and residence times under nitrogen atmosphere. FTIR, Polarized Light Microscopy, XRD and SEM were employed to characterize MP, indicating that the coal tar pitch was transformed into MP through dehydrogenative condensation reactions. The optimum yield was found at 400℃ and 7h
参考文献
| [1] | Otani S .Mechanism of the carbonization of MP carbon fiber at the low temperature range[J].CARBON,1967,5(03):219-220. |
| [2] | Oskar Paris;Dieter Loidl;Herwig Peterlik .Texture of PAN-and pitch-based carbon fibers[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(4):551-555. |
| [3] | Fujiura R;Kojima T;Mochida I et al.Evaluation of naphthalene-derived mesophase pitches as a binder for carbon-carbon composites[J].Carbon,1993,31(01):97-107. |
| [4] | Maeda T;Zeng S M;Takumitsu K et al.Preparation of isotropic pitch precursors for general purpose carbon fibers(GPCF)by air blowing-I. Preparation of spinnable isotropic pitch precursor from coal tar by air blowing[J].Carbon,1993,31(03):407-412. |
| [5] | Osamu Ito .UV-visible and near-IR spectra of heat-treated pitches during mesophase formation[J].Carbon,1993,31(03):401-406. |
| [6] | Hutchenson K W;Roebers J R;Thies M C .Fractionation of petroleum pitch by supercritical fluid extraction[J].CARBON,1991,29(02):215-223. |
| [7] | Hüttinger K J;Wang J P .Kinetics of mesophase formation in a stirred tank reactor and properties of the products - II. Discontinuous reactor[J].Carbon,1992,30(01):1-8. |
| [8] | Singer L S .Carbon fibers from mesophase pitch[J].Fuel,1981,60:839-847. |
| [9] | Brooks J D;Tayler G H .The formation of graphitizing carbons from the liquid phase[J].Carbon,1965,3(02):185-186. |
| [10] | Lowery H H .Chemistry of coal utilization[Z].Wiley New Yark,1963. |
| [11] | Diefendorf R J;Riggs D M .Forming optically anisotropic pitches[P].United State Patent: US4 208 267,1980. |
| [12] | Barr J B;Chwastiak S;Singer L S .High modulus carbon fibers from pitch precursor[J].Applied Polymer Symposium,1976,29:161-173. |
| [13] | Wang CY.;Wu YL.;Guo CT.;Li MW. .Preparation and microstructure of hollow mesophase pitch-based carbon fibers[J].Carbon: An International Journal Sponsored by the American Carbon Society,1998(12):1749-1754. |
| [14] | M. BRAUN;K. J. HUETTINGER .SINTERING OF POWDERS OF POLYAROMATIC MESOPHASE TO HIGH-STRENGTH ISOTROPIC CARBONS: Ⅲ. POWDERS BASED ON AN IRON-CATALYZED MESOPHASE SYNTHESIS[J].Carbon: An International Journal Sponsored by the American Carbon Society,1996(12):1473-1491. |
| [15] | Sang-Hee Park;Kap-Seung Yang;Soon Young Soh .Preparation of partial mesophase pitch-based carbon fiber from FCC-DO[J].Carbon,2001,39(02):99-104. |
| [16] | Mustafa Z O;Kieth D B .Production of mesophase from coal-tar and petroleum pitches using supercritical fluid extraction[J].Turkish Journal of Chemistry,2002,26:417-424. |
| [17] | Lewis I C;Singer L S.The formation of mesophase from acenaphthylene: Kinetic and free radical studies[A].Pennsylvania, Pittsburgh,1975:265-267. |
| [18] | Brooks J D;Tayler G H;Walker Jr P L .Chemistry and Physics of Carbon[C].Arnold London and M.Dekker,New Yark,1968,4E:243. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%