制备出问苯二胺、间苯二酚改性三聚氰胺甲醛树脂.利用红外光谱测试表征产物的结构;通过热失重仪和差示扫描量热器测定了树脂的热失重率以及相变焓,研究了改性后树脂的热稳定性的变化.结果表明,经过化学改性后,三聚氰胺甲醛树脂分子引入苯环结构,使树脂在300℃左右的热稳定性得到提高.
参考文献
| [1] | Cho J S;Kwon A;Cho C G .Microencapsulation of octadecane as a phase-change material by intedacial polymerization in an emulsion system[J].Colloid and Polymer Science,2002,280:260. |
| [2] | Masahiro A;Hideki I;Yoshinobu F .Microencapsulation of water-soluble macromolecules with acrylic terpolymers by the Wurster coating process for colon-specific drug delivery[J].Powder Technology,2004,141(02):177. |
| [3] | Kim J;Cho G .Thermal storage/release durability,and temperature sensing properties of thermostatic fabrics treated with oetadecane-containing microcapsules[J].Textile Research Journal,2002,72(12):1093. |
| [4] | 任晓亮,王立新,任丽,苏峻峰.原位聚合法制备相变储热微胶囊[J].功能材料,2005(11):1722-1724,1727. |
| [5] | Sun G;Zhang Z .Mechanical strength of microcapsules made of different wall materials.[J].International Journal of Pharmaceutics,2002(1/2):307-311. |
| [6] | 杨惊,沈一丁.三聚氰胺甲醛树脂及其衍生物的研究现状与应用前景[J].化工时刊,2004(12):12-15. |
| [7] | 宫克.三聚氰胺甲醛树脂合成与性能的研究[J].沈阳化工,1996(04):25. |
| [8] | 琚晓晖,齐鲁.有机硅改性三聚氰胺甲醛树脂的性能[J].纤维复合材料,2006(01):12-14. |
| [9] | 杨中兴,齐鲁,狄海燕.三聚氰胺甲醛树脂改性及其纤维的性能[J].高分子材料科学与工程,2008(01):147-150. |
| [10] | 余丽蓉,陆春华,高树军,许仲梓.十二醇/三聚氰胺-甲醛核壳结构材料的制备[J].南京工业大学学报（自然科学版）,2007(02):6-10. |
| [11] | 贺鹏,齐鲁.改性三聚氰胺树脂纤维性能的研究[J].高分子材料科学与工程,2007(01):165-168. |
| [12] | Critchley J P;Knight G J;Wright W W.Heat-resistant polymers[M].New York:Plenum Press,1983:34. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%