介绍硅烷预处理反应机理,对预处理液中的主要影响因素通过正交实验进行研究,找出最佳工艺参数.预处理后喷涂丙烯酸粉末涂层,通过附着力、乙酸铜盐雾试验和FILIFORM试验检查涂层性能.结果表明:预处理液中硅烷浓度8 g/L,添加剂浓度1.0 g/L,pH =2.0,反应时间2 min为最优条件,硅烷预处理能显著提高铝合金表面丙烯酸粉末涂层的附着力和耐腐蚀性.
参考文献
| [1] | TAN Y J;BAILEY S;KINSELLA B .Studying the formation process of chromate conversion coatings on aluminum using continuous electrochemical noise resistance measurements[J].Corrosion Science,2002,44(06):1277-1286. |
| [2] | Directive 2002/95/EC of the european parliament and the council on the restriction of the use of certain hazardous substances in electrical and electronic equipments[J].Official Journal of the European Communities,2003(37):19-33. |
| [3] | 李文刚,张晓丰,吕勤秀,左禹.LF21铝合金稀土转化膜的开裂及其钼酸盐后处理[J].腐蚀与防护,2009(04):248-250,275. |
| [4] | 郭瑞光,杨杰,康娟.铝合金表面钛酸盐化学转化膜研究[J].电镀与涂饰,2006(01):46-48. |
| [5] | 王成,江峰,林海潮,姜喜奎.铝合金铈盐转化膜的研究[J].电镀与涂饰,2001(01):24-26. |
| [6] | HINTON B R W .The inhibition of aluminum corrosion by cerium cations[J].Metals Forum,1984,7(04):211-217. |
| [7] | 于兴文,曹楚南,林海潮,周育红,周德瑞,尹钟大.Al6061/SiCp稀土转化膜的组成、结构及性能[J].物理化学学报,2000(06):547. |
| [8] | 闫斌,陈宏霞,陈嘉宾.功能性有机硅烷膜对金属腐蚀防护的研究现状及展望[J].材料保护,2009(03):54-57. |
| [9] | 张小琴.铝合金硅烷化表面处理技术现状[J].材料研究与应用,2011(03):177-180. |
| [10] | 赵平,孙广霞,杨玉鹏,王宏,张发余.有机硅烷偶联剂在涂装前处理中的应用[J].电镀与精饰,2010(03):25-28. |
| [11] | 刘倞,胡吉明,张鉴清,曹楚南.金属表面硅烷化防护处理及其研究现状[J].中国腐蚀与防护学报,2006(01):59-64. |
| [12] | 王雪明,李爱菊,李国丽,管从胜.硅烷偶联剂在防腐涂层金属预处理中的应用研究[J].材料科学与工程学报,2005(01):146-150. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%