以煤系高岭石为原料,经粉磨、煅烧活化后加入碱性激发剂,在常温常压条件下制备出了具有早强、高强性能的土聚水泥.正交优化设计了高岭土的煅烧温度和保温时间、Na2O·nSiO2溶液的掺量和模数等对土聚水泥抗压强度的影响.研究表明:煤系高岭土经850℃煅烧、保温2h,所得的处于无定型状态的偏高岭土经模数为1.2、掺量为9%Na2O·nSiO2溶液的激发,可制备出4h抗压强度达87.5MPa,7d强度达137.6MPa的新型胶凝材料.
参考文献
| [1] | 唐明述.节能减排工作应重视提高基建工程寿命[J].中国水泥,2007(09):24-28. |
| [2] | Davidovits J .The ancient Egyptian Pyramids-concrete or rock[J].Concrete International,1987,9(12):28. |
| [3] | Davidovits J .Geopolymers:Inorganic polymer new materials[J].Journal of Thermal Analysis,1991,37:1633. |
| [4] | Davidovits J.Geopolymer chemistry and properties[A].Compiegne:The Geopolymer Institute,1988:25. |
| [5] | Davidovits J .Geopolymers:Man-made rock geosynthesis and the resuhion development of very early high strength cement[J].J Mater Educ,1994,16(2-3):91. |
| [6] | Davidovits J .Recent progresses in concretes for nuclear waste and uranium waste containment[J].Concrete International,1994,16(12):53. |
| [7] | 代新祥,文梓芸.土聚水泥的应用及研究现状[J].水泥,2001(10):11-14. |
| [8] | 吴怡婷,施惠生.制备土聚水泥中若干因素的影响[J].水泥,2003(03):1-3. |
| [9] | 王玉江,李和平,任和平.土聚水泥的研究[J].硅酸盐通报,2003(04):70-74. |
| [10] | 孙凤金,陶文宏,付兴华,杨忠喜.地聚物胶凝材料制备工艺的研究[J].山东建材,2007(01):16-20. |
| [11] | Barbosa V F F;iVhckemie K J D;Thaumaturgo C.Synthesis and characterisation of materials based on inorganic polymers of alumina and silica:sodium polysialate polymers[J].International Journal of Inorganic Materials,2000(02):309. |
| [12] | 曹德光,苏达根,宋国胜.低模数硅酸钠溶液的结构及其键合反应特性[J].硅酸盐学报,2004(08):1036-1039. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%