采用了两种不同的充氢方法(浸泡充氢和高压气相热充氢)研究了氢对断口上颗粒状亮区(Granular Bright Facet/GBF)尺寸的影响.研究表明,浸泡充氢并没有改变“GBF”的颗粒状特征,高压气相热充氢使得“GBF”的颗粒状特征变浅甚至消失.不论哪种充氢方法,充氢均使得“GBF”在较低的外加载荷下出现,且与充氢前相比“GBF”尺寸明显增加.电化学充氢没有改变疲劳寿命与(SGBF)1/2/(Sinc)1/2之间的关系,但是高压气相热充氢后疲劳寿命与(SGBF)1/2/(Sinc)1/2之间的关系有显著变化.
参考文献
[1] | 洪友士,赵爱国,钱桂安.合金材料超高周疲劳行为的基本特征和影响因素[J].金属学报,2009(07):769-780. |
[2] | 李永德,郭卫民,徐娜,吴晓峰,时军波,马虹.SUJ2轴承钢超声疲劳GBF内裂纹扩展规律[J].材料热处理学报,2014(01):49-54. |
[3] | 周承恩,谢季佳,洪友士.超高周疲劳研究现状及展望[J].机械强度,2004(05):526-533. |
[4] | 王清远,刘永杰.结构金属材料超高周疲劳破坏行为[J].固体力学学报,2010(05):496-503. |
[5] | 胡燕慧,张峥,钟群鹏,韩邦成.金属材料超高周疲劳研究进展[J].机械强度,2009(06):979-985. |
[6] | 鲁连涛,张卫华.金属材料超高周疲劳研究综述[J].机械强度,2005(03):388-394. |
[7] | 李守新;翁宇庆;惠卫军.高强度钢超高周疲劳性能-非金属夹杂物的影响[M].北京:冶金工业出版社,2010:1-6. |
[8] | Stanzl S E;Tschegg E K;Mayer H .Lifetime measurements for random loading in the very high cycle fatigue range[J].International Journal of Fatigue,1986,8:195-200. |
[9] | Murakami Y;Yokoyama N N;Nagata J .Mechanism of fatigue failure in uhralong life regime[J].Fatigue Fracture Engineering Materials Structure,2002,25:735-746. |
[10] | Bathias C;Paris P C.Gigacycle Fatigue in Mechanical Practice[M].New York:Marcel Dekker,Inc,2005:1-7. |
[11] | 王毛球,董瀚,惠卫军,时捷,秋山英二,津崎兼彰.氢对高强度钢缺口拉伸强度的影响[J].材料热处理学报,2006(04):57-60. |
[12] | Yongde Li;Zhenguo Yang;Shouxin Li;Yangbo Liu;Shuming Chen;Weijun Hui;Yuqing Weng .Effect of Hydrogen on Fatigue Strength of High-Strength Steels in the VHCF Regime[J].Advanced Engineering Materials,2009(7):561-567. |
[13] | Nakajima M;Tokaji K;Itoga H et al.Morphology of step-wise S-N curves depending on work-hardened layer and humidity of a high strength steel[J].Fatigue and Fracture Engineering Materials Structure,2003,26:1113-1118. |
[14] | Tokaji K.;Ko HN.;Nakajima M.;Itoga H. .Effects of humidity on crack initiation mechanism and associated S-N characteristics in very high strength steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):197-206. |
[15] | Murakami Y;Nomoto T;Ueda T et al.On the mechanism of fatigue failure in the superlong life regime (Nf 》 107 cycles).Part I:Influence of hydrogen trapped by inclusions[J].Fatigue and Fracture Engineering Materials Structure,2000,23:893-902. |
[16] | Murakami Y;Matsunaga H .The effect of hydrogen on fatigue properties of steels used for fuel cell system[J].International Journal of Fatigue,2006,28:1509-1021. |
[17] | 钱桂安,洪友士.环境介质对40Cr结构钢高周和超高周疲劳行为的影响[J].金属学报,2009(11):1356-1363. |
[18] | Shi J B;Li Y D;Guo W M et al.On effect of hydrogen on very high cycle fatigue behaviors of high strength steels[J].Materials Science and Technology,2013,29(11):1290-1296. |
[19] | 褚武扬;乔立杰;陈奇志.断裂与环境断裂[M].北京:科学出版社,2000:95-109. |
[20] | Nakatani, M.;Fujihara, H.;Sakihara, M.;Minoshima, K. .Fatigue crack growth acceleration caused by irreversible hydrogen desorption in high-strength steel and its mechanical condition[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011(25/26):7729-7738. |
[21] | Maoqiu Wang;Eiji Akiyama;Kaneaki Tsuzaki .Hydrogen Degradation of a Boron-Bearing Steel with 1050 and 1300 Mpa Strength Levels[J].Scripta materialia,2005(5):403-408. |
[22] | Shiozawa K;Lu L;Ishihara S .S-N curve characteristics and subsurface crack initiation behaviour in uhra-long life fatigue of a high carbon-chromium bearing steel[J].Fatigue and Fracture Engineering Materials Structure,2001,24:781-790. |
[23] | Li, YD;Chen, SM;Liu, YB;Yang, ZG;Li, SX;Hui, WJ;Weng, YQ .The characteristics of granular-bright facet in hydrogen pre-charged and uncharged high strength steels in the very high cycle fatigue regime[J].Journal of Materials Science,2010(3):831-841. |
[24] | Liu, Y.B.;Li, S.X.;Li, Y.D.;Yang, Z.G. .Factors influencing the GBF size of high strength steels in the very high cycle fatigue regime[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011(3):935-942. |
[25] | Chapetti M D;Tagawa T;Miyata T .Ultra-long cycle fatigue of high-strength carbon steels part Ⅱ:estimations of fatigue limit for failure from internal inclusions[J].Materials Science and Engineering A,2003,356:236-244. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%