脉冲磁场下,以7055Al-Ce2（CO3）3为反应体系制备了内生Al2O3颗粒增强铝基复合材料。X射线衍射仪（XRD）、扫描电镜（SEM）、电子探针（EPMA）分析表明,在脉冲磁场作用下,原位合成的颗粒细小,呈球形或橄榄形的Al2O3颗粒尺寸为200～400nm,且弥散分布于基体中。从反应动力学角度进行考虑,与常规反应相比,磁场下反应更快更完全,并缩短了反应时间。随着脉冲磁场强度的增大,反应生成的增强颗粒变得更加细小,分布更均匀。当磁场作用的时间增加时,内生颗粒数目逐渐增多,尺寸逐渐细化,圆钝化,分布也变得均匀,颗粒达到纳米尺寸。
Under pulsed magnetic field,7055 aluminum matrix composites reinforced by in-situ Al2O3 particles had been fabricated successfully from 7055 Al-Ce2（CO3）3 system.The results indicate that in-situ particles synthesized under pulsed magnetic field are finer and uniformly dispersed in the aluminum matrix.The range of round and Al2O3 particles size is 200-400nm.Compared with traditional in-situ reaction,the in situ reaction under pulsed magnetic field is faster and more complete,and shorten time considering the reactive kinetics.With the increasing of the plused magnetic intensity and applying time,the size and distribution of in-situ particles in the matrix become finer and more homogenous,the size is up to nanomete.
参考文献
| [1] | 汪小燕,赵玉涛,陈刚,程晓农,张红杰,章照.Al-K2ZrF6体系熔体反应法合成复合材料的微观组织和力学性能[J].稀有金属材料与工程,2007(02):259-263. |
| [2] | 赵玉涛,孙国雄.Al-ZrOCl2反应体系制备ZrAl3（p）+Al2O3（p）/Al复合材料[J].中国有色金属学报,2001(01):41-46. |
| [3] | 许可,赵玉涛,陈刚,张松利.脉冲磁场下原位合成（Al2O3+Al3Zr）p/Al复合材料的微观组织及力学性能[J].中国有色金属学报,2007(04):607-611. |
| [4] | 周晓霞,张仁元,刘银峁.稀土元素在铝合金中的作用和应用[J].新技术新工艺,2003(04):43-45. |
| [5] | 吕佳娉,索掌怀.几种铈盐的热分解过程及非等温热分解动力学研究[J].烟台大学学报（自然科学与工程版）,2006(02):117-124. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%