目的：了解干热环境条件对聚苯乙烯表面结构及性能的影响。方法在吐鲁番和敦煌大气环境中对聚苯乙烯进行1年自然曝晒试验，研究聚苯乙烯表面黄色指数、微观结构随暴露时间的变化规律。结果在干热大气环境中，随暴露时间延长，聚苯乙烯表面黄色指数增加，出现裂纹，老化过程中有C O和O-C O基团生成。结论聚苯乙烯在干热大气环境中的老化主要由光氧化引起的链断裂和羰基增加造成。
Objective To find out the effects of dry-heat environment on the surface structure of polystyrene. Methods The ex-posure test of polystyrene( PS) was carried out for one year in Tulufan and Dunhuang. The changes of surface morphology and chemical structures were studied by spectrophotometry, fourier transform infrared ( FTIR) spectroscopy and X-ray photoelectron spectroscopy. Results Cracks on polystyrene surface were observed and yellow index was increased with prolonging exposure time. Organo-functional group CO and O-CO were found during the aging period. Conclusion Photodegradation of polystyrene in dry-heat environment was induced by chain break and increase in carbonyl group.
参考文献
| [1] | 刘鑫,揭敢新,陶友季,胡利芬,郭燕芬,马坚,王俊,冯皓.自然环境老化对聚苯乙烯表观性能和形态的影响[J].塑料工业,2013(01):83-86. |
| [2] | 聚苯乙烯光氧老化行为及其模型研究[J].塑料科技,2013(01):53-56. |
| [3] | 郭燕芬,陶友季,马坚,揭敢新,张晓东,胡利芬,刘鑫,王俊.湿热环境户外自然老化对PS分子结构的影响[J].塑料,2013(03):108-112. |
| [4] | 易平,何建新,杨秀清,杨德模.3种高分子材料自然环境多角度暴露对比试验[J].表面技术,2007(02):18-20. |
| [5] | 揭敢新,王俊,张晓东,彭坚.高分子材料用于我国大气环境严酷度比较的研究[J].装备环境工程,2012(06):10-12,35. |
| [6] | Sousa AR;Amorim KLE;Medeiros ES;Melo TJA;Rabello MS .The combined effect of photodegradation and stress cracking in polystyrene[J].Polymer Degradation and Stability,2006(7):1504-1512. |
| [7] | 何建新,李继红,胡滨,文静.改性聚苯乙烯材料自然环境老化研究[J].表面技术,2008(05):26-28. |
| [8] | Jose Salas Vicente;Juan Lopez Gejo;Sonja Rothenbacher .Oxidation of polystyrene aerosols by VUV-photolysis and/or ozone[J].Photochemical & photobiological sciences: the official journal of the European Photochemistry Association and the European Society for Photobiology,2009(7):944-952. |
| [9] | 萧以德,王光雍,李晓刚,林安,张三平,秦晓洲,王振尧,梁彩凤,郑弃非,毛海荣.我国西部地区大气环境腐蚀性及材料腐蚀特征[J].中国腐蚀与防护学报,2003(04):248-255. |
| [10] | 张三平,萧以德.应重视西部环境对材料的腐蚀--西部环境腐蚀状况调查[J].材料保护,2002(07):58-60. |
| [11] | 马艳秋;王仁辉;刘树华.材料自然老化手册[M].北京:中国石化出版社,2004 |
| [12] | YE Rong-gen,肖春霞,CAI Xu-fu,李光宪.苯乙烯树脂抗老化研究进展[J].塑料,2008(04):72-75. |
| [13] | 魏薇,肖敏,何建新.军用包装箱材料自然环境老化XPS研究[J].装备环境工程,2008(05):42-44,57. |
| [14] | 宣卫芳,王一临,胥泽奇.弹药塑料包装材料自然环境老化现象研究[J].装备环境工程,2006(05):26-30. |
| [15] | 钟世云;许乾慰;王公善.聚合物降解与稳定化[M].北京:化学工业出版社,2002 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%