This paper presents the effects of aging processes on the properties and microstructure of Cu-0.3Cr-0.15Zr-0.05Mg lead frame alloy. Optimal conditions for good hardening and electrical conductivity can be obtained by solution treating at 920℃ for lh and aging at 470℃ for 4h and at 550℃ for lh. The hardness and electrical conductivity can reach 108HV, 73%IACS and 106HV, 76%IACS, respectively. Aging precipitation was dealt with by transmission electronic microscope (TEM). At 470℃ aging for 4h the fine precipitation of an ordered compound CrCu2(Zr, Mg) is found in matrix as well as fine Cr and Cu4Zr. Aging at 550℃ for lh some precipitates are still coherent with matrix. The CrCu2(Zr, Mg) completely dissolves into Cr and Cu4Zr.
参考文献
| [1] | Ryu H J;Baik H K .Effect of thermomechanical treatment on microstructure and properties of Cu-base leadframe alloy[J].Journal of Materials Science,2000,35:3641-3646. |
| [2] | SU Juan-hua;DONG Qi-ming;LIU Ping .Simulation of aging process of lead frame copper alloy by an artificial neural network[J].Transactions of Nonferrous Metals Society of China,2003(6):1419-1423. |
| [3] | Batra IS.;Kulkarni UD.;Banerjee S.;Dey GK. .Microstructure and properties of a Cu-Cr-Zr alloy[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2001(2):91-100. |
| [4] | Qi WX.;Tu JP.;Liu F.;Yang YZ.;Wang NY.;Lu HM.;Zhang XB.;Guo SY. Liu MS. .Microstructure and tribological behavior of a peak aged Cu-Cr-Zr alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):89-96. |
| [5] | Huang Fuxiang;Ma Jusheng;Ning Honglong;Geng Zhiting;Lu Chao;Guop Shumei;Yu Xuetao;Wang Tao;Li Hong;Lou Huafen .Analysis of phases in a Cu-Cr-Zr alloy[J].Scripta materialia,2003(1):97-102. |
| [6] | Holzwarth U.;Stamm H. .The precipitation behaviour of ITER-grade Cu-Cr-Zr alloy after simulating the thermal cycle of hot isostatic pressing[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2000(1):31-45. |
| [7] | Kang BX;Cao XG;Huang JL;Yen B;Gu HC;Liu P .Aging precipitation and recrystallization of rapidly solidified Cu-Cr-Zr-Mg alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(1/2):262-267. |
| [8] | Tang N Y et al.Precipitation and aging in high-conductivity Cu-Cr alloys with additions of zirconium and magnesium[J].材料科学与工艺(英文版),1985,1:270-270. |
| [9] | Batawi E;Morris D G;Morris M A .Effect of small alloying additions on behavior of rapidly solidified Cu-Cr alloysp[J].材料科学与工艺(英文版),1990,6:892-899. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%