Cu(OH)2 nano-fibers were prepared by chemical precipitation with CuSO4·5H2O and NaOH as raw materials.The Cu(OH)2 nano-fibers have a diameter of 10-30 nm and a length of 1-6 μm. The reaction conditions were as follows: the concentration of CuSO4 solution was 0.1 mol·L-1, NaOH solution 4 mol·L-1, the dropping rate of the NaOH solution 50 mL·min-1, the reaction temperature 20℃, the pH value of the reaction terminal 13, and the stirring rate 1200 r·min-1. The chain nano-CuO grains were obtained through the microwave radiation of the Cu(OH)2 nano-fibers.

参考文献

[1] Larsson PO.;Andersson A. .Complete oxidation of CO, ethanol, and ethyl acetate over copper oxide supported on titania and ceria modified titania[J].Journal of Catalysis,1998(1):72-89.
[2] Zhang R B;Liu H Y;Li F S .Study on preparation of the composite nano materials[J].Acta Detonator,2000,23(01):59.
[3] Zhong X .Widely usable antimicrobial of nano copper oxide[J].New Mater Chem Eng,2003,31(12):46.
[4] Li D S;Wang W L;Wang X Y .Preparation of CuO powders through solid synthesis of the predecessor at the room temperature[J].Functional Materials,2003,6(34):723.
[5] Hong W L;Zhao F Q;Liu J H .A new method to prepare nano-CuO[J].Acta Detonator,2000,23(03):7.
[6] Fendler J H;Dekany I.Nanoparticles in Solids and Solutions[M].Netherlands:kluwer Academic Publishers,1996:191.
[7] Kumar R V;Diamant Y;Gedanken A .Sonochemical synthesis and characterization of nanometer-size transition metal oxides from metal acetates[J].Chemistry of Materials,2000,12:2301.
[8] Carnes CL.;Stipp J.;Klabunde KJ. .Synthesis, characterization, and adsorption studies of nanocrystalline copper oxide and nickel oxide[J].Langmuir: The ACS Journal of Surfaces and Colloids,2002(4):1352-1359.
[9] Fan Z L;Jia Z J .Study on preparing method of nano-copper oxide of self-separation and anti-ageing[J].Acta Artif Cryst,2003,32(04):356.
[10] Puntes V F;Krishnan K M;Alivisatos A P .Colloidal nanocrystal shape and size control:the case of cobalt[J].Science,2001,291:2115.
[11] Zhu Q Y;Li S F .Preparation of nano-CuO powders by microwave[J].Aviat Missile,2002,9:59.
[12] J H Huang,N A Rowson.An Application of Microwave Pre-oxidation in Improving Gold Recovery of a Refractory Gold Ore[J].稀有金属(英文版),2000(03):161-171.
[13] ZHANG Haijun,WU Xiangwei,JIA Quanli,JIA Xiaolin.Synthesis and microwave characterization of Co-SiC core-shell powders by electroless plating[J].稀有金属(英文版),2006(03):216-220.
[14] ZHANG Maisheng.Rapid Synthesis of Submicrometer-sized Red Phosphor CaS∶Cu+,Eu2+ in a Microwave Field[J].稀有金属(英文版),2000(04):279-284.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%