采用基本断裂功法对共聚聚丙烯压制双边缺口拉伸试样的断裂行为进行研究,分析了厚度变化对材料多项断裂参数的影响.结果表明,当厚度在0.6 mm～1.1 mm时,材料的断裂韧性we随厚度增大呈现出明显的下降趋势,下降幅度约30%,主要由屈服后的we,n降低所致, 屈服前的we,y无明显变化;材料的比塑性功βwp随厚度增大未呈现明显的变化,且屈服前的βywp,y和屈服后的βnwp,n均无明显变化.同时求得了外推的零韧带断裂位移e0,b和最大载荷P0,y,随厚度增大,前者具有一定的下降趋势,后者则显示出较大的增长趋势.
参考文献
| [1] | Mai Y M;Cotterell B;Horlyck R;Vigna G .[J].Polymer Engineering and Science,1987,27:804. |
| [2] | Test Protocol for Essential Work of Fracture,Version 5[M].ESIS TC-4 Group,Les Diablerets,1998 |
| [3] | Gong G;Xie BH;Yang W;Li ZM;Zhang WQ;Yang MB .Essential work of fracture (EWF) analysis for polypropylene grafted with maleic anhydride modified polypropylene/calcium carbonate composites[J].Polymer Testing,2005(4):410-417. |
| [4] | Maspoch M L;Ferrer D;Cordillo A et al.[J].Journal of Applied Polymer Science,1999,73:177-187. |
| [5] | Hashemi S .[J].POLYMER,2002,43:4033-4041. |
| [6] | Maspoch M L;Perez J G;Gordillo A et al.[J].POLYMER,2002,43:4177-4183. |
| [7] | 谢邦互,沈岳新,李忠明,杨伟,冯建民,杨鸣波.聚丙烯/POE共混组成对材料断裂行为的影响[J].高分子学报,2006(02):335-339. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%