采用溶胶凝胶工艺,在ITO透明导电玻璃基板上成功地制备了Zn掺杂的Pb0.4Sr0.6TiO3(PST)铁电薄膜.XRD结果表明:550℃和600℃不同热处理条件下烧结的薄膜均呈单一的钙钛矿相结构.在不同外加直流电场下测试Zn 掺杂PST薄膜的介电性能,研究薄膜的介电可调性与热处理温度及过程的关系.发现550℃条件下制备得到的Zn掺杂PST薄膜几乎没有介电可调性,而在600℃条件下制备的Zn掺杂PST薄膜具有明显的介电可调性.另外,600℃条件下制备的Zn掺杂PST薄膜,其可调性随着保温时间和冷却时间的延长有所增加,介电损耗随保温时间和冷却时间的增大而减小.
参考文献
| [1] | 王季魁,沈明荣,方亮,甘肇强.溶胶-凝胶法制备钛酸锶铅薄膜和多层膜及其介电性质[J].功能材料,2006(02):231-233,237. |
| [2] | Lee S G;Kim C I;Kim B C .[J].Journal of the European Ceramic Society,2004,24:157. |
| [3] | Park J;Lu J W;Boesch D S et al.[J].IEEE Microwave & Wireless Components Letter,2006,16(05):264. |
| [4] | Lee Y C.[A].Manchester:European Microwave Society,2006:1347. |
| [5] | Hao JH;Gao J;Wong HK .Laser molecular beam epitaxy growth and properties of SrTiO3 thin films for microelectronic applications[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2006(2):559-562. |
| [6] | Zhai J W;Shen B;Yao X et al.[J].Materials Research Bulletin,2004,39:1599. |
| [7] | de los santos Guerra J;Garcia D;Eiras J A et al.[J].Journal of the European Ceramic Society,2005,25:2089. |
| [8] | Genderen P V.[J].Airborne Radar,2005(01):42. |
| [9] | Somiya Y;Bhalla A S;Cross L E.[J].International Journal of Inorganic Materials,2001(03):709. |
| [10] | 杜丕一,隋帅,翁文剑,韩高荣,汪建勋.Mg掺杂PST薄膜的溶胶-凝胶法制备及晶相形成研究[J].物理学报,2005(11):5411-5416. |
| [11] | 丁子上.硅酸盐物理化学[M].北京:中国建筑工业出版社,1980:293. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%