采用常压干燥法制备了SiO2气凝胶,所得气凝胶为介孔结构,比表面积618.8m2/g,孔径分布5～20nm.以SiO2气凝胶为原料,通过静电吸附法制备了SiO2气凝胶/壳聚糖复合药物载体材料,采用扫描电镜(SEM)、红外光谱(FTIR)等对复合材料的结构形貌进行了分析,研究了复合材料对硫酸庆大霉素药物的担载和释放性能.结果表明,所得SiO2气凝胶/壳聚糖复合材料为多孔网络结构,其中,由450℃处理的SiO2气凝胶制得的气凝胶/壳聚糖复合材料对硫酸庆大霉素具有较好的药物担载和缓释性能.
参考文献
| [1] | 张启焕,江昕,闫玉华,陈晓明.多孔β-TCP陶瓷药物载体结构与性能的影响因素[J].佛山陶瓷,2003(09):33-34. |
| [2] | 王德平,黄文显,陈天丹.多孔微晶玻璃作为药物载体材料的制备及其体外释药研究[J].无机材料学报,2001(06):1195-1198. |
| [3] | Smirnova I;Suttiruengwong S;Arlt W .Feasibility study of hydrophilic and hydrophobic silica aerogels as drug delivery systems[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2004(0):54-60. |
| [4] | Pirjo K;Manja A;Stefan K et al.[J].Journal of Biomedical Materials Research,1999,44(02):162-167. |
| [5] | Ahola MS;Sailynoja ES;Raitavuo MH;Vaahtio MM;Salonen JI;Yli-Urpo AU .In vitro release of heparin from silica xerogels.[J].Biomaterials,2001(15):2163-2170. |
| [6] | 姜炜,李凤生,杨毅,刘宏英,楚建军.磁性壳聚糖复合微球的制备和性能研究[J].材料科学与工程学报,2004(05):660-662. |
| [7] | Sivakumar M;Manjubala I;Panduranga Rao K .[J].Carbohydrate Polymers,2002,49:281-288. |
| [8] | Yang YM;Wang JW;Tan RX .Immobilization of glucose oxidase on chitosan-SiO2 gel[J].Enzyme and Microbial Technology,2004(2):126-131. |
| [9] | Ayers M R;Hunt Arlon J .[J].Journal of Non-Crystalline Soilds,2001,285:123-127. |
| [10] | 史非,王立久.环境气压干燥新工艺快速合成SiO2气凝胶研究[J].大连理工大学学报,2006(02):241-245. |
| [11] | Shi F;Wang L J;Liu J X.[J].Journal of Materials Science and Technology |
| [12] | 朱以华,答鸿,杨晓玲,胡英.SiO2微球表面吸附PDADMAC的研究[J].化学物理学报,2004(06):775-778. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%