Application of Stereology on Neodymium-Doped Yttrium Aluminum Garnet (Nd: YAG) Transparent Ceramics

稀土学报(英文版), 2006, 24(5): 538-542.

^1, , ^2, , ^3, , ^4, , ^5, , ^6, , ^7,

1.School of Materials and Chemical Engineering, Changchun University of Science and Technology, Changchun 130022, China

2.Chinese Special Vehicle Institute, Beijing 100072, China

3.School of Materials and Chemical Engineering, Changchun University of Science and Technology, Changchun 130022, China

4.School of Materials and Chemical Engineering, Changchun University of Science and Technology, Changchun 130022, China

5.School of Materials and Chemical Engineering, Changchun University of Science and Technology, Changchun 130022, China

6.School of Materials and Chemical Engineering, Changchun University of Science and Technology, Changchun 130022, China

7.School of Materials and Chemical Engineering, Changchun University of Science and Technology, Changchun 130022, China

基金项目: Key Science and Technology of Chinese Ministry of Education(205037)

Application of Stereology on Neodymium-Doped Yttrium Aluminum Garnet (Nd: YAG) Transparent Ceramics

Keywords： neodymium doped yttrium aluminum garnet

Nd: YAG precursor powders were synthesized by homogeneous precipitation, and Nd: YAG transparent ceramics were prepared by vacuum sintering at 1700 ℃ for 5 h. The ceramic materials were characterized by light transmittance and field emission gun-environment scanning microscope. Using statistics and stereology theory, study was carried out on the quantitative relationships between light transmittance and stereological parameters in three-dimensional Euclidean space. It is found that the transmittance of Nd:YAG with 1 mm in thickness is about 45% and 58% in visible and near-infrared wavelength, respectively. The transmittance linearly increases with increasing equivalent sphere diameter and reaches the theoretical value of single crystal when the equivalent sphere diameter is 20μm. The transmittance decreases with the increasing of mean specific area per unit volume of grain and discrete grains, and the transmittance decreases with increasing mean free distance of grains in Nd:YAG ceramics.

参考文献

[1]	Su Chunhui;Zhang Huashan;Han Hui .Preparation of Neodymium-Doped Yttrium Aluminum Garnet Transparent Ceramics by Homogeneous Precipitation Method[J].Journal of Rare Earths,2005(6):716-720.
[2]	Zhang Huashan,Su Chunhui,Han Hui,Hou Zhaoxia.Synthesis of Neodymium-Doped Yttrium Aluminum Garnet (Nd∶YAG) Nano-Sized Powders by Low Temperature Combustion[J].稀土学报（英文版）,2005(03):304-308.
[3]	Ervin E Underwood.Quantitative Stereology[M].MA:Addsion-Wesley,1970
[4]	John C Russ;Robert T Dehoff.Practical Stereology[M].New York:Kluwer Academic,2000
[5]	Li J M;Lü Li.Image-Based Fractal Description of Microstructures[M].New York:Kluwer Academic,2003
[6]	Sekita M;Haneda H;Yanagitani T et al.Induced emission cross section of Nd:Y3Al5O12 ceramics[J].Journal of Applied Physics,1990,67(01):453.
[7]	Masami Sekita;Hajime Haneda;Shirasaki et al.Optical spectra of undoped and rare-earth (= Pr,Nd,Eu,and Er)-doped transparent ceramics Y3Al5O12[J].Journal of Applied Physics,1991,69(06):3709.
[8]	Ikesue A.;Kamata K.;Yoshida K.;Kinoshita T. .FABRICATION AND OPTICAL PROPERTIES OF HIGH-PERFORMANCE POLYCRYSTALLINE ND-YAG CERAMICS FOR SOLID-STATE LASERS[J].Journal of the American Ceramic Society,1995(4):1033-1040.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Application of Stereology on Neodymium-Doped Yttrium Aluminum Garnet (Nd: YAG) Transparent Ceramics

参考文献