利用光学金相显微镜研究了GH4700合金在冷轧以及中间退火过程中的组织演变规律,建立了中间退火过程中再结晶晶粒长大方程.实验结果表明:随着冷轧变形量增大,晶粒的变形均匀性逐渐变好,GH4700合金的屈服强度和抗拉强度增大,延伸率降低；当退火温度为1130℃、保温时间为15 min时,组织发生完全再结晶且分布均匀,是较合适的一次冷轧中间退火工艺；所建立的晶粒长大模型预测结果与试验值吻合较好.
参考文献
| [1] | Christopher J. Cowen;Paul E. Danielson;Paul D. Jablonski .The Microstructural Evolution of Inconel Alloy 740 During Solution Treatment, Aging, and Exposure at 760℃[J].Journal of Materials Engineering and Performance,2011(6):1078-1083. |
| [2] | Viswanathan R;Coleman K;Rao U .Materials for ultra-supercritical coal-fired power palnt boilers[J].International Journal of Pressure Vessels and Piping,2006,83(11-12):778. |
| [3] | N.D. Evans;P.J. Maziasz;R.W. Swindeman .Microstructure and phase stability In INCONEL alloy 740 during creep[J].Scripta materialia,2004(6):503-507. |
| [4] | 赵双群,董建新,张麦仓,谢锡善.新型镍基高温合金在950℃和1000℃的氧化行为[J].稀有金属材料与工程,2005(02):208-211. |
| [5] | S.J. Patel.INTRODUCTION TO INCONEL ALLOY 740: AN ALLOY DESIGNED FOR SUPERHEATER TUBING IN COAL-FIRED ULTRA SUPERCRITICAL BOILERS[J].金属学报（英文版）,2005(04):479-488. |
| [6] | 孔学云,王宝峰,金自力,任慧平,张晓燕.冷轧板再结晶退火中组织和织构演变的研究[J].材料热处理学报,2007(04):97-101. |
| [7] | 计云萍,金自力,任慧平,王玉峰,孙昊.CSP工艺冷轧薄板盐浴退火再结晶实验[J].钢铁研究学报,2008(11):43-46,62. |
| [8] | 陈礼清,隋凤利,刘相华.Inconel 718合金方坯粗轧加热过程晶粒长大模型[J].金属学报,2009(10):1242-1248. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%