以Ni包覆Ti粉末为原始粉末,采用低温超音速火焰喷涂(low temperature High Velocity Oxygen Fuel,LT-HVOF)工艺沉积了Ti-Ni涂层.采用SEM、XRD等分析了Ti-Ni涂层显微结构和相组成,探讨了热处理工艺对涂层的相组成和显微结构影响.结果表明,在950℃×5 h下单质Ti与Ni完全合金化为NiTi(B2),Ni3Ti及Ti2Ni.在950℃×5 h+850℃×1h+水冷,涂层中NiTi(B2)结晶度更高,涂层均匀致密.
参考文献
| [1] | Halter K;Ickinger A;Siegmann S.Thermal spray forming of NiTi shape memory alloys[A].United States of America,2004 |
| [2] | Corrosion performance of HVOF and APS thermally sprayed NiTi intermetallic coatings in 3.5% NaCl solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(3):1052. |
| [3] | M. Bram;A. Ahmad-Khanlou;H.P. Buchkremer;D. Stoever .Vacuum plasma spraying of NiTi protection layers[J].Materials Letters,2002(3):647-651. |
| [4] | 王德政,周克崧,杨大君,曾爱群,王建荣,施洪波.低压等离子喷涂Ti-Ni合金涂层工艺的研究[J].广东有色金属学报,1991(01):39. |
| [5] | Wang H T;Li C J;Yang G J.Formation of NiTi intermetallics by heat treatment of cold-sprayed precursor coating[A].陕西西安,2009 |
| [6] | 戴达煌;周克崧;袁镇海.现代材料表面技术科学[M].北京:冶金工业出版社,2004 |
| [7] | 周克崧,邓春明,邓畅光,刘敏.Ti-Ni低温超音速火焰喷涂层及激光处理后的特征[J].材料保护,2009(08):62-63,82. |
| [8] | Deng C M;Liu M;Deng C G et al.Preparation and characterizations of NiTi intermetallic coatings[J].Current Advances in Materials and Processes,2011,291-294:80-83. |
| [9] | Zhou Y;Yang J.Phase formation in cold-Spray Ni/Ti coating during Annealing Treatment[A].陕西西安,2009 |
| [10] | 叶人伦;胡建华.实用无机物热力学数据手册(第二版)[M].北京:冶金工业出版社,2002 |
| [11] | 李松瑞;周善初;田荣璋.金属热处理[M].长沙:中南大学出版社,2003 |
| [12] | 王洪铎 .NiTi金属间化合物涂层的制备及形成机理研究[D].西安:西安石油大学,2009. |
| [13] | Zhu S I;Yang X I;Fu L Y;elt al .Stress-strain behavioror of porous NiTi alloys prepared by powers sintering[J].Materials Science and Engineering A,2005,408(12):264-268. |
| [14] | Bastin G F;Rieck.G D .Diffusion in the Titanium-Nickel System:Ⅱ.Calculations of Chemical and Intrinsic diffusion Coefficients[J].Metallurgical and Materials Transactions,1974,5:1827-1831. |
| [15] | 周勇,杨冠军,吴限,李长久.层叠Ni/Ti热扩散形成金属间化合物的规律[J].焊接学报,2010(09):41-44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%