以硝酸锆-尿素为原料,采用溶液燃烧合成(SCS)法制备了超细ZrO2粉末,着重研究了后续煅烧处理对合成的ZrO2粉末结构、尺寸和团聚程度的影响.结果表明,利用SCS法可以合成超细ZrO2粉末,对之进一步进行煅烧处理,可明显降低合成产物中残留有机物的含量,并改善合成粉末的分散性;在700℃煅烧1.0h的条件下,可以获得分散性好,粒径小(＜200nm)的ZrO2粉末.
参考文献
| [1] | Gutknecht D;Chevalier J;Garnier V et al.[J].Journal of the European Ceramic Society,2007,27(2-3):1547-1552. |
| [2] | 梁丽萍,张磊,盛永刚,徐耀,吴东,孙予罕,蒋晓东,魏晓峰.溶胶-凝胶ZrO2-TiO2高折射率光学膜层的抗激光损伤性能研究[J].物理学报,2007(06):3596-3601. |
| [3] | Archer T;Pemmaraju C D;Sanvito S .[J].Journal of Magnetism and Magnetic Materials,2007,316(02):188-190. |
| [4] | Liu J;Zhao Z;Xu C et al.[J].Catalysis Communications,2007,8(03):220-224. |
| [5] | S. BIAMINO;P. FINO;M. PAVESE .Alumina-zirconia-yttria nanocomposites prepared by solution combustion synthesis[J].CERAMICS INTERNATIONAL,2006(5):509-513. |
| [6] | Kameswari U;Sleight A W;Evans J S O .[J].International Journal of Inorganic Materials,2000,2(04):333-337. |
| [7] | Chen Z;Yan Y W .[J].Journal of Materials Science,2006,41(17):5793-5796. |
| [8] | 陈哲,严有为.PDP用纳米BaMgAl10O17：Eu荧光粉的燃烧合成及发光性能[J].物理化学学报,2006(08):1030-1033. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%