研究了在真空电弧炉和快淬炉2种快速凝固条件下制备的Gd5Si2Ge2合金的显微组织与相组成.结果表明,Gd5Si2Ge2合金在电弧炉熔炼条件下,具有不同质量的样品可以获得不同的显微组织与相组成.不同速度下,快淬甩带实验表明,在小于40m/s的快淬速度下,Gd5Si2Ge2合金为单斜Gd5Si2Ge2-型晶体结构;在50m/s的快淬速度下Gd5Si2Ge2合金包含Gd5Si4-型和Gd5Si2Ge2-型两相.证实了冷却速度对Gd5Si2Ge2合金的相组成有重要影响.
参考文献
| [1] | Gordon S Smith;Tharp A G;Quintin Johson.[J].NATURE,1966:1148. |
| [2] | Holtzberg F;Gambino R J;Meguire T R.[J].Journal of Physics and Chemistry of Solids:2283. |
| [3] | Pecharsky VK;Gschneidner KA .Tunable magnetic regenerator alloys with a giant magnetocaloric effect for magnetic refrigeration from similar to 20 to similar to 290 K[J].Applied physics letters,1997(24):3299-3301. |
| [4] | Pecharsky V K;Gschneidner Jr K A.[J].Journal of Magnetism and Magnetic Materials,1997:1179. |
| [5] | Pecharsky V K;Gschneidner K A Jr.[J].Journal of Applied Physics,1999(08):5365. |
| [6] | Pecharsky A O;Pecharsky V K;Gschneidner K A Jr.[J].Journal of Alloys and Compounds,2002:126. |
| [7] | Pecharsky A O;Gschneidner K A Jr;Pecharsky V K.[J].Journal of Applied Physics,2003(08):4722. |
| [8] | 付浩,陈云贵,唐永柏,涂铭旌.Gd5Si2Ge2/Gd室温磁制冷复合材料激光熔覆成形工艺研究[J].稀有金属材料与工程,2003(05):387-389. |
| [9] | 吴卫,赵平,姜自莲,李远辉,朱向东,周廷栋.原材料Gd对Gd-Si-Ge合金巨磁热效应影响的研究[J].稀有金属材料与工程,2003(11):962-964. |
| [10] | Szade J.;Winiarski A.;Skorek G. .Surface structure of Gd-5(Si,Ge)(4) crystals[J].Journal of Crystal Growth,1999(3):289-293. |
| [11] | Meyers J S;Chumbley L S;Laabs F.[J].Scripta Materialia,2002:509. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%