采用内氧化法以水雾化铜铝粉为原料制备出铝含量(质量分数)分别为0.15%、0.40%、0.60%的Al_2O_3弥散铜复合材料.研究了Al_2O_3弥散强化铜材料的组织与性能,结果表明,弥散铜材料的晶粒细小,晶粒大小约为10μm;γ-Al_2O_3在基体中均匀分布,平均尺寸约为6mm,间距为40nm;挤压态为Al含量0.60%的弥散铜棒材(Φ25mm)不经任何中间热处理,直接冷拉拔即可得到Φ3mm的铜丝,其抗拉强度高达680MPa,电导率达78%IACS.
Series of aluminum oxide dispersion strengthened copper composite(ODSC) containing 0.15%,0.4%,0.6% Al(wt%) are produced from water atomized Cu-Al powder through internal oxidation.The microstructure and properties of the composite are researched.The results show that the grain of the ODSC alloy is very small with a size of 10μm.γ-Al_2O_3 nano-particles with the mean size of 6 nm are uniformly distributed in the matrix grain and space distance between particles is about 40nm.Without any intermediate heat treatment,the copper wires with 0.60% Al with Φ3mm in diameter are produced by direct cold drawing from the hot extruded bar with Φ25mm in diameter.The tensile strength of these copper wires is 680MPa,the electrical conductivity is 78% IACS.
参考文献
| [1] | Song Kexing et al.Optimization of the processing parameters during internal oxidation of Cu-Al alloy powders using an artificial neural network[J].Materials & Design,2005,26:337. |
| [2] | 程建奕,汪明朴,李周,方善峰,郭明星,刘施峰.纳米Al2O3粒子弥散强化铜合金冷加工及退火行为[J].稀有金属材料与工程,2004(11):1178-1181. |
| [3] | 宁爱林,申奇志,雷先明,彭北山.弥散强化铜的研制现状与展望[J].邵阳高等专科学校学报,2001(03):165-166. |
| [4] | T.S. Srivatsan;Meslet Al-Hajri;J.D. Troxell .The tensile deformation, cyclic fatigue and final fracture behavior of dispersion strengthened copper[J].Mechanics of materials,2004(1/2):99-116. |
| [5] | 程建奕,汪明朴,钟卫佳,王艳辉,李周,洪斌,熊晓明,曹先杰.内氧化法制备的Cu-Al2O3合金的显微组织与性能[J].材料热处理学报,2003(01):23-27. |
| [6] | 申玉田;崔春翔 et al.高强度高导电Cu-Al_2O_3复合材料的制备[J].金属学报,1999,35(08):888. |
| [7] | 张家敏,亢若谷,彭茂公,田卫平,刘辉,单玉友.产业化制备弥散强化铜材料的性能及工艺研究[J].云南冶金,2004(06):25-30. |
| [8] | Besterci M.;Ivan J. .The mechanism of the failure of the dispersion-strengthened Cu-Al2O3 system[J].Journal of Materials Science Letters,1998(9):773-776. |
| [9] | Song Kexing;Xing Jiandong;Dong Qiming et al.Internal oxidation of dilute Cu-Al alloy powers with oxidant of Cu_2O[J].Materials Science and Engineering,2004,A380:117. |
| [10] | 谢文果;谢学智 .弥散强化铜合金中强化质点的形态结构和粒度[J].粉末冶金技术,1996,14(02):136. |
| [11] | 申玉田,孙建忠,崔春翔,徐艳姬,张宏标,戚玉敏.Cu-Al合金内氧化产物及分布的研究[J].粉末冶金技术,2004(03):131-134. |
| [12] | Su-Hyeon Kim;Dong Nyung Lee .Recrystallization of alumina dispersion strengthened copper strips[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1/2):24-33. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%