近年来,随着风电行业的快速发展,叶片后缘粘接开裂成为一种主要的失效形式.因此,后缘粘接胶理想宽度的模拟成为一种必要.计算结果表明,后缘实体粘接胶最理想的粘接宽度范围为100～150mm.
参考文献
| [1] | 中国风电能否继续高歌猛进[J].电气制造,2011(02) |
| [2] | 顾怡红 .风力发电机叶片优化设计方法研究[D].浙江大学,2014. |
| [3] | 刘克明,金莹,康林萍,谌昀,付青峰.复合材料的细观力学研究进展[J].江西科学,2010(03):354-358. |
| [4] | 习年生,于志成,陶春虎.纤维增强复合材料的损伤特征及失效分析方法[J].航空材料学报,2000(02):55-63. |
| [5] | M. A. Eder;R. D. Bitsche;M. Nielsen;K. Branner .A practical approach to fracture analysis at the trailing edge of wind turbine rotor blades[J].Wind energy,2014(3):483-497. |
| [6] | Adams RD;Comyn J;Wake WC.Structural adhesive joints in engineering[M].London:Chapman and Hall,1997 |
| [7] | Gleich DM;Van Tooren MJL;Beukers A .Analysis and evaluation of bondline thickness effects on failure load in adhesively bonded structures[J].Adhes.Sci.Technol,2001,15:1091-1101. |
| [8] | Sen Yang.An experimental study on the dependence of the strength of adhesively bonded joints with thickness and mechanical properties of the adhesives[J].Journal of Adhesion Science and Technology |
| [9] | M. A. Eder;R. D. Bitsche;M. Nielsen;K. Branner .A practical approach to fracture analysis at the trailing edge of wind turbine rotor blades[J].Wind energy,2014(3):483-497. |
| [10] | 李军向.复合材料层合板失效分析[M].北京:机械工业出版社,2014 |
| [11] | 刘军,李英梅,黄宝宗.复合材料层板损伤失效分析[J].东北大学学报（自然科学版）,2006(01):76-79. |
| [12] | 刘克明,金莹,康林萍,谌昀,付青峰.复合材料的细观力学研究进展[J].江西科学,2010(03):354-358. |
| [13] | 谈娟娟,贾智源,宋秋香.风电叶片用结构胶粘剂粘度及触变性试验分析[J].玻璃钢/复合材料,2013(03):26-29. |
| [14] | 周伟.风电叶片复合材料结构缺陷无损检测研究进展[J].玻璃钢/复合材料,2013 |