以对苯二胺(PDA)和联苯四甲酸二酐(BPDA)为单体,合成了聚酰亚胺前驱体——聚酰胺酸溶液.采用溶液共混法将氧化石墨烯与聚酰胺酸复合,经制膜和热酰亚胺化反应制备了石墨烯/聚酰亚胺复合薄膜.用红外光谱(FT-IR)、拉曼光谱(Raman)、X射线衍射(XRD)和扫描电镜(SEM)对复合材料的结构和形态进行了分析.发现被还原的氧化石墨烯已经充分剥离并均匀分散在聚酰亚胺基体中,且与基体树脂结合紧密.力学性能测试表明,石墨烯的加入明显改善了聚酰亚胺的拉伸强度,当石墨烯含量为2％时,复合材料的拉伸强度提高了53％.热失重分析发现,复合薄膜的热稳定性也得到明显改善,相对于纯的聚酰亚胺,添加2％石墨烯的复合材料其热降解温度提高了10℃.
参考文献
| [1] | Bolotin, KI;Sikes, KJ;Jiang, Z;Klima, M;Fudenberg, G;Hone, J;Kim, P;Stormer, HL .Ultrahigh electron mobility in suspended graphene[J].Solid State Communications,2008(9/10):351-355. |
| [2] | Balandin AA;Ghosh S;Bao WZ;Calizo I;Teweldebrhan D;Miao F;Lau CN .Superior thermal conductivity of single-layer graphene[J].Nano letters,2008(3):902-907. |
| [3] | Changgu Lee;Xiaoding Wei;Jeffrey W. Kysar;James Hone .Measurement of the Elastic Properties and Intrinsic Strength of Monolayer Graphene[J].Science,2008(5887):385-388. |
| [4] | Stoller MD;Park SJ;Zhu YW;An JH;Ruoff RS .Graphene-Based Ultracapacitors[J].Nano letters,2008(10):3498-3502. |
| [5] | Jishan Wu;Wojciech Pisula;Klaus Mullen .Graphenes as Potential Material for Electronics[J].Chemical Reviews,2007(3):718-747. |
| [6] | 徐伟华,韦春,刘红霞,余传柏,苏乐,曾思华.氧化石墨烯/酚醛树脂原位复合材料的热性能和动态力学性能[J].高分子材料科学与工程,2013(05):79-82. |
| [7] | Stankovich S;Dikin DA;Dommett GHB;Kohlhaas KM;Zimney EJ;Stach EA;Piner RD;Nguyen ST;Ruoff RS .Graphene-based composite materials[J].Nature,2006(7100):282-286. |
| [8] | 谢卫刚,赵东林,景磊,张凡.石墨烯/环氧树脂复合材料的制备与力学性能[J].高分子材料科学与工程,2012(09):129-132. |
| [9] | Li X;Wang X;Zhang L;Lee S;Dai H .Chemically derived, ultrasmooth graphene nanoribbon semiconductors.[J].Science,2008(5867):1229-1232. |
| [10] | Zhao, X;Zhang, QH;Chen, DJ;Lu, P .Enhanced Mechanical Properties of Graphene-Based Poly(vinyl alcohol) Composites[J].Macromolecules,2010(5):2357-2363. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%