利用铝酸酯偶联剂F-1对金红石型纳米TiO2进行干法改性.采用红外光谱(FT-IR)、紫外-可见分光光度计(UV-Vis)、接触角测试及扫描电镜(SEM)对纳米TiO2的改性效果进行了表征.以改性纳米TiO2作为紫外吸收助剂,研究了其时粉末涂料抗紫外光老化性能的影响.结果表明,铝酸酯偶联剂F-1是有效的改性剂,改性后的纳米TiO2具有疏水性,从而提高了其在粉末涂料中的分散性能.通过1368 h人工加速老化发现,随着纳米TiO2含量的增加,纳米改性粉末涂料的耐候性能得到较大提高.当纳米TiO2质量分数为2.0%时,光泽度保持率可提高34.7%,色差减小27.3%.
参考文献
| [1] | 郭刚,汪斌华,黄婉霞,于杰,曹建军,涂铭旌.纳米TiO2的紫外光学特性及在粉末涂料抗老化改性中的应用[J].四川大学学报(工程科学版),2004(05):53-56,61. |
| [2] | Li ZW.;Zhu YF. .Surface-modification of SiO2 nanoparticles with oleic acid[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2003(1/4):315-320. |
| [3] | Masayoshi Fuji;Takashi Takei;Tohoru Watanabe;Masatoshi Chikazawa .Wettability of fine silica powder surfaces modified with several normal alcohols[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,1999(1/2):13-24. |
| [4] | Rene J. Nussbaumer;Walter Caseri;Theo Tervoort;Paul Smith .Synthesis and characterization of surface-modified rutile nanoparticles and transparent polymer composites thereof[J].Journal of nanoparticle research: An interdisciplinary forum for nanoscale science and technology,2002(4):319-323. |
| [5] | 姚超,吴凤芹,林西平,杨绪杰,陆路德,汪信.超声场中纳米TiO2表面包覆氧化硅的研究[J].无机化学学报,2005(01):59-64. |
| [6] | Jim R.White .Polymer ageing:physics,chemistry or engineering?Time to reflect[J].Comptes Rendus Chimie,2006(11/12):1396-1408. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%