在A3钢表面Zn-Fe合金电镀液中加入镧盐,研究La3+对Zn-Fe合金镀层在酸性介质中腐蚀行为的影响.用线性扫描伏安法和电化学阻抗法,研究Zn-Fe合金镀层在30℃的0.20 mol/L H2SO4溶液中的腐蚀行为.用XRD和SEM研究Zn-Fe合金镀层在腐蚀前后的微观结构和形貌的变化.结果表明,加入镧盐没有改变Zn-Fe合金镀层的晶面择优取向,但影响各晶面衍射峰强度,使镀层结晶粒度变小;当加入La2(SO4)3为0.90 g/L时,Zn-Fe合金镀层变得致密均匀,电结晶生长形态呈现层状;镀层的致钝电流密度(ipp)和维钝电流密度(ip)显著降低,极化电阻Rp增大,镀层具有良好的耐蚀性能.
参考文献
| [1] | I. H. Karahan;H. A. Cetinkara;H. S. Guder .Electrodeposition and characterisation of Zn, Zn-Fe and Zn-Fe-Ni coatings in presence of gelatin as additive[J].Transactions of the Institute of Metal Finishing: The International Journal for Surface Engineering and Coatings,2008(3):157-161. |
| [2] | V. Thangaraj .Electrodeposition and corrosion behaviour of some Zn-Fe group metal alloys by pulsed current[J].Transactions of the Institute of Metal Finishing: The International Journal for Surface Engineering and Coatings,2009(4):208-216. |
| [3] | Barbosa LL;Carlos IA .Development of a novel alkaline zinc-iron plating bath containing sorbitol and the chemical, physical and morphological characterization of the Zn-Fe films[J].Surface & Coatings Technology,2006(3/4):1695-1703. |
| [4] | Lee KK;Lee IH;Lee CR;Ahn HK .In-situ observation in a scanning electron microscope on the exfoliation behavior of galvannealed Zn-Fe coating layers[J].Surface & Coatings Technology,2007(14):6261-6266. |
| [5] | 张茂才,周寿增,王亦忠,Hadjipanayis G C.铸造RE-Fe-（C,B）合金的组织结构与磁性[J].中国稀土学报,2001(05):411-413. |
| [6] | 张新明,王文韬,刘波,陈明安,刘瑛,高志国,叶凌英,贾寓真.Nd对2519铝合金组织与耐热性能的影响[J].中国有色金属学报,2009(01):15-20. |
| [7] | 陈亚军,许庆彦,黄天佑.稀土铝钛硼中间合金的细化能力与长效性[J].中国有色金属学报,2007(08):1232-1239. |
| [8] | 王晓秋,丁伟中,王新国,张静江.混合稀土对ZL108铝合金组织与性能的影响[J].中国稀土学报,2004(02):243-246. |
| [9] | 章江洪,张英杰,陈阵,范云鹰.稀土铈在锌-铁合金电沉积中的作用[J].中国稀土学报,2003(z1):157-159. |
| [10] | 汪兵,刘清友,王向东,贾书君,卢吉,董瀚.稀土Ce和La对碳钢在NaCl溶液中的缓蚀机理[J].中国腐蚀与防护学报,2007(03):151-155. |
| [11] | 曹超,鲁道荣.钒对Zn-Fe合金镀层耐蚀性的影响[J].材料保护,2007(08):12-14,23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%