采用惰性气体蒸发和原位真空压结法制备了具有清洁界面的纳米PbF2块材．通过X射线衍射、差热分析和复平面阻抗谱方法，研究了相结构、相变和离子电导率．结果表明，纳米PbF2比粗晶PbF2的离子电导率大幅提高，相变温度降低了30℃.
The bulk samples of nanophase PbF2(n-PbF2) with the clean interfaces were prepared by using an inert gas evaporation and in situ compacting technique. The phase constitution and ionic conductivity were studied by XRD, DSC and complex impedance spectra. The results show that the ionic conductivity of n-PbF2 is rather higher than that of coarse-grained PbF2. The temperature of phase transition from α-phase to β-phase for n-PbF2 drops about 30℃ compared with that of coaxse-grained PbF2.
参考文献
| [1] | Allnatt A, Chadwick A V, Jacobs P W M. Proc. R. Soc. London, 1987, Ser. A410: 385--390. [2] Lucat C, Campet G, Claverie J, et al. Mat. Res. Bull., 1976, 11: 162--172. [3] Wu X J, Su F, Qin X Y, et al. Mater. Res. Soc. Symp. Proc., 1993, 286: 27--32. [4] 苏方，吴希俊, 秦晓英等. 科学通报， 1993， 38 (3)： 221--223. [5] Puin W, Heitjans P. Nanostructured Mater., 1995, 6: 885--889. [6] 黄胜涛主编. 固体X射线学. 北京：高等教育出版社， 1985, 197--234. [7] Liang C C, Joshi A V. J. Electrochem. Soc., 1976, 123: 466--470. [8] Benz R. Z Physik. Chem. Neue Folge, Bd. 95: 25--32. [9] Kennedy J H, Miles R, Hunter J. J. Electrochem. Soc., 1973, 120: 1441--1446. [10] Horvath J, Birringer R, Gleiter H. Solid State Commun., 1987, 62: 319--322. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%