TiO2纳米阵列超疏水膜的制备及耐腐蚀性能

腐蚀学报（英文）, 2012, 24(1): 37-40.

TiO2纳米阵列超疏水膜的制备及耐腐蚀性能

薛超瑞 ^1, , 董丽华 ^2, , 刘通 ^3, , 张芬 ^4, , 尹兵 ^5, , 尹衍升 ^6,

1.上海海事大学海洋材料科学与工程研究院,上海,201306

2.上海海事大学海洋材料科学与工程研究院,上海,201306

3.上海海事大学海洋材料科学与工程研究院,上海,201306

4.上海海事大学海洋材料科学与工程研究院,上海,201306

5.上海海事大学海洋材料科学与工程研究院,上海,201306

6.上海海事大学海洋材料科学与工程研究院,上海,201306

基金项目: 上海市科技项目(10170502400) 海洋局项目(201005028-4) 青岛市重点基金(09-1-3-38-jch)

关键词： TiO2纳米管 , 超疏水 , 阳极氧化 , 耐腐蚀性

Preparation and Anticorrosion Performance of Superhydrophobic TiO2 Nanotube Arrays on Pure Ti

Keywords： TiO2 nanotube , superhydrophobic , anodization , anticorrosion

采用阳极氧化法在纯钛表面制备TiO2纳米管阵列，使用六甲基二硅胺烷对TiO2纳米管阵列进行低表面能处理，得到超疏水表面．用接触角测量仪测定表面疏水性，采用SEM、EDS技术研究改性前后试样表面的形貌和元素组成，并利用极化曲线和电化学阻抗谱法研究了超疏水膜的耐腐蚀性能．结果表明，TiO2纳米管阵列经改性后超疏水效果明显，耐腐蚀性能大幅度提高．

Superhydrophobic TiO2 nanotube arrays on pure Ti was prepared by surface- modification in Hexamethyldisilazane （HMDS） solution and its performance, surface morphology and composition were characterized by means of water contact angle measurement, energy dispersive X-ray spectrum （EDS） and scanning electron microscopy （SEM）. The corrosion behavior of the superhydrophobic surface film was investigated with potentiodynamic polarization measurements and electrochemical impedance spectroscopy（EIS）. The results showed that the superhydrophobic surface film significantly decreased the corrosion currents densities （Icorr）, and increased the polarization resistance （Rt） of Ti. Due to the air valleys and capillarity effects, the corrosion resistance of the material was improved remarkably.

参考文献

[1]	Quere D. Non-sticking drops[J]. Rep. Prog. Phys., 2005, 68(11): 2495.
[2]	Barthlott W, Neinhuis C. The purity of sacred lotus or escape from contamination in biological surfaces[J]. Planta, 1997, 202(1): 1.
[3]	Neinhuis C, Barthlott W. Characterization and distribution of water-repellent, self-cleaning plant surfaces [J]. Ann. Bot., 1997, 79(6): 667.
[4]	Zhang J L, Li J A, Han Y C. Superhydrophobic PTFE surfaces by extension [J]. Macromol. Rapid. Commun., 2004, 25(11): 1105.
[5]	Manoudis P N, Karapanagiotis L, Tsakalof A, et al. Su- perhydrophobic composite films produced on various sub- strates[J]. Langmuir, 2008, 24(19): 11225.
[6]	Hedge N D, Rao A V. Organic modification of TEOS based silica aerogels using hexadecyltrimethoxysilane as a hydrophobic reagent[J]. Appl. Surf. Sci., 2006, 253(3): 1566.
[7]	Wang B, Feng J, Gao C Y. Surface wettability of compressed polyelectrolyte multilayers[J]. Colloids Surf. A: Physicochem. Eng. Aspects, 2005, 259: 1.
[8]	江雷,冯琳.仿生智能纳米界面材料[M].北京:化学工业出版社,2005.
[9]	刘世凯.TiO2基纳米管阵列的构筑、表征及光电化学性质研究[D].长春:吉林大学,2009.
[10]	范丽颖,刘俊玲,安红.钛在海洋工程上的应用现状及前景展望[J].中国金属通报,2006,39-40:25.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网