以溶液聚合法合成了2种不同组成的羟基丙烯酸树脂,研究了引发剂、反应温度与共聚物组成对共聚物相对分子质量、羟值和聚合体系黏度的影响.采用六亚甲基二异氰酸酯(HDI)三聚体分别与2种羟基丙烯酸树脂进行交联固化,并表征了树脂及其交联固化涂膜的机械性能、耐化学试剂性能和热稳定性.结果表明:共聚物组成中苯乙烯的加入明显降低了聚合体系的黏度,提高了树脂固含量,改善了涂膜物理性能.通过对引发剂用量、聚合反应温度、反应单体配比的控制,成功地制备出固含量为70％,综合性能优良的羟基丙烯酸树脂.
参考文献
| [1] | M.Slinckx;N.Henry;A.Krebs;G.Uytterhoeven .High-Solids Automotive Coatings[J].Progress in Organic Coatings: An International Review Journal,2000(3/4):163-173. |
| [2] | KEITH D W .Paint and coatings:a mature industry in transition[J].Progress in Polymer Science,1997,22(02):203-245. |
| [3] | KAMATH V R;SARGENT J D .Production of high solids acrylic coating resins with t-amyl peroxides:a new way to meet VOC requirements[J].Journal of Coatings Technology,1987,59(746):51-56. |
| [4] | Peters CA;Ellwood KR;Srivastava Y;Nichols ME;Greenfield ML .Ultraviolet light absorber mobility in crosslinked coatings: Experiments and modeling[J].Progress in Organic Coatings: An International Review Journal,2007(4):272-281. |
| [5] | 方冉,耿志远,张兴辉,高敬民,陈延辉,梁义芳.双组分高固体丙烯酸聚氨酯涂料的研究[J].涂料工业,2005(01):7-11. |
| [6] | Charles A. Zezza;Kimberly D. Talmo .Viscosity Reduction via Monomer Selection in Solvent-Borne High-Solids Styrene/Acrylic Coating Resins[J].JCT,1996(856):49-54. |
| [7] | YOSHIO E;ATSUSHI Y;KYOTO .Acrylic resin composition for use in high solids paints[P].US,4687822,1987-08-18. |
| [8] | AIBERT I;KENDALL P;MICHAEL G et al.High solids acrylic-based coatings[P].US,4985517,1991-01-15. |
| [9] | 全国表面活性剂洗涤用品标准化中心.表面活性剂和洗涤剂国际标准汇编[M].北京:中国轻工业出版社,1996 |
| [10] | 潘祖仁.高分子化学[M].北京:化学工业出版社,2007:111-134. |
| [11] | 郐羽,牟洋,孙赫,张会轩.官能化丙烯酸酯类涂料树脂的制备及性能研究[J].涂料工业,2012(05):32-35,40. |
| [12] | 夏正斌 .高性能丙烯聚氨酯涂料及其涂膜干燥模型的研究[D].华南理工大学,2000. |
| [13] | 高家武.高分子材料热分析曲线集[M].北京:科学出版社,1990:68-77. |
| [14] | 林燕宜;李耀荣 .热重法测定紫外光辐射固化漆膜的交联度[J].中山大学学报(自然科学版),1994,33(04):128-131. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%