将电火花线切割316奥氏体不锈钢试样在450℃下进行气体渗氮8h.分析原始面和线切割面渗氮后的显微组织、渗层相结构及元素分布,并对其硬度、耐磨性和耐蚀性进行测试.结果表明,线切割面渗氮后得到了更厚的渗层,渗层由S相(扩展奥氏体相)组成,渗氮后硬度和耐磨性大幅提高,而耐蚀性基本不变.线切割促进渗氮的原因在于电火花加工过程中快速冷却形成表层马氏体,促进活性氮原子的快速扩散.
参考文献
| [1] | 林峰,梁东,邢海生,陈战.奥氏体不锈钢耐蚀渗氮工艺的研究[J].热处理,2010(02):27-30. |
| [2] | R.R.M. de Sousa;F.O. de Araujo;J.C.P. Barbosa .Nitriding using cathodic cage technique of austenitic stainless steel AISI 316 with addition of CH_4[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):124-127. |
| [3] | Toshkov V;Russev R;Madjarov T et al.On low temperature ion nitriding of austenitic stainless steel AISI 316[J].Joural of Achievements in Materials and Manufacturing Engineering,2007,25(01):71-74. |
| [4] | Thomas Bell .Current status of superstaturated surface engineered S-phase materials[J].Key Engineering Materials,2008,373-374:289-295. |
| [5] | Tong W P;Liu C Z;Wang W et al.Gaseous nitriding of iron with a nanostructured surface layer[J].Scripta Materialia,2007,57:533-536. |
| [6] | 葛利玲,路彩虹,井晓天,卢正欣.40Cr钢表面纳米化对气体渗氮行为的影响[J].材料热处理学报,2008(05):155-159. |
| [7] | 闫牧夫,刘瑞良,吴业琼,杨茂.纳米化3J33钢低温渗氮生成相性能第一性原理表征[J].材料热处理学报,2009(02):167-171. |
| [8] | Ferkel H;Glatzer M;Estrin Y et al.RF plasma nitriding of a severely deformed high alloy steel[J].Scripta Materialia,2002,46(09):623-628. |
| [9] | Ji SJ;Wang L;Sun JC;Hei ZK .The effects of severe surface deformation on plasma nitriding of austenitic stainless steel[J].Surface & Coatings Technology,2005(1):81-84. |
| [10] | 赵宪,王存山.激光硬化和渗氮复合处理W9Mo3Cr4V高速钢组织与性能[J].中国激光,2012(07):102-107. |
| [11] | 李茅坪.高速钢电火花线切割加工白亮层的研究[J].电加工与模具,2004(03):36-38. |
| [12] | 葛利玲,卢正欣,井晓天,刘忠良,田娜.0Cr18Ni9不锈钢表面纳米化组织及其热稳定性对低温渗氮行为的影响[J].金属学报,2009(05):566-572. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%