The high-temperature, high-pressure hot isostatic pressing technology was used for depositing hard coatings on Ti(C, N)-based cermets. The microstructure and properties of the sample were investigated using optical microscopy, scanning electron microscopy, X-ray diffraction, electron probe microanalysis, and microhardness tester. The results showed that the rich titanium and nitrogen in surface zone were induced by the heat treatment. The high nitrogen activity of the surface region was the driving force for outward transport of titanium and inward transport of tungsten in the cobalt binder. The toughness and hardness were improved and a hardness gradient was formed. It is the high-temperature, high-pressure N2that enables closure of holes, thereby alleviating defects and prolonging tool life.
参考文献
| [1] | Zeng D L.Powder Metallurgy Material[M].北京:冶金工业出版社,1989:152. |
| [2] | Xiong W H.Study on Microstructure and Interface Structure of the Grain Complex Hard Material[M].武汉:华中理工大学出版社,1994:31. |
| [3] | Zackrisson J;Rolander U;Weinl G;Andren H.O .Microstructure of the surface zone in a heat-treated cermet material[J].International Journal of Refractory Metals and Hard Materials,1998,16:315. |
| [4] | Zackrisson J.;Rolander U. .MICROSTRUCTURE AND PERFORMANCE OF A CERMET MATERIAL HEAT-TREATED IN NITROGEN[J].Acta materialia,2000(17):4281-4291. |
| [5] | Grzesik W .The role of coatings in controlling the cutting process when turning with coated indexable inserts[J].Journal of Materials Processing Technology,1998,79:133. |
| [6] | Cselle T;Barimani A .Today's applications and future developments of coatings for drills and rotating cutting tools[J].Surface and Coatings Technology,1995,76:712. |
| [7] | Ettmayer P;Kolaska H;Lengauer W;Dreyer K .Ti(C,N) Cermets-metallurgy and properties[J].International Journal of Refractory Metals and Hard Materials,1995,13:343. |
| [8] | 吴玉萍,林萍华,王泽华.等离子熔覆原位合成TiC陶瓷颗粒增强复合涂层的组织与性能[J].中国有色金属学报,2004(08):1335-1339. |
| [9] | Shetty D;Wright I;Mincer P .Indentation fracture of WC-Co cermets[J].Journal of Materials Science,1985,20:1873. |
| [10] | Subramanian C;Strafford K N .Review of multicomponent and multilayer coatings for tribological applications[J].Wear,1993,165:85. |
| [11] | Audy J;Strafford K N;Subramanian C .The efficiency of uncoated and coated tool systems in the machining of low carbon steel assessed trough cutting force measurements[J].Surface and Coatings Technology,1995,76-77:706. |
| [12] | 郑勇,熊惟皓,宗校军,余立新,李国安.Ti（C,N）基金属陶瓷功能梯度材料的制备[J].粉末冶金技术,2002(04):195-199. |
| [13] | 郑勇,熊惟皓,宗校军,余立新,李国安.Ti（C,N）基金属陶瓷氮化处理后的表面组织结构及形成机理[J].硅酸盐学报,2003(03):262-267. |
| [14] | Konyashin I Y .Activated nitriding of TiCN-based cermets[J].Surface and Coatings Technology,1995,73:125. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%