以钛酸四丁酯为钛源,氨水为沉淀剂,采用水解-沉淀法制备出了氮掺杂纳米TiO2催化剂(N/TiO2),以XRD、DRS、PL、FTIR、SEM、TEM等手段对所制备的粉体进行了性能表征;并以目光色镝灯为光源,研究了催化剂对光降解甲基橙的活性.XRD结果表明,除了700℃煅烧样品是锐钛矿和金红石晶型共存外,其它N掺杂催化剂主要是锐钛矿晶型.DRS蛄果显示,不同温度煅烧的催化荆在波长低于550nm的可见光区城内都有高的吸光度.先催化结果发现,700℃煅烧制得的N掺杂氧化钛光催化荆表现出最佳的光催化活性,120min内对甲基橙溶液的降解率达到69.7%.
N-doped nano-TiO2 photocatalyst(N/TiO2) was prepared by hydrolysis-deposition method with tetra-butyl titanate and ammonia as the precursors, The as-prepared N/TiO2 powders were characterized by XRD,DRS, PL, FTIR, SEM and TEM, the photocatalytic activity of as-prepared photocatalyst was studied by degrada-tion of a model methyl orange solution using solar color dysprosium lamp as a light source, the results of XRD showed that N/TiO2 samples were in the form of anatase style other than the sample calcined at 700℃ ,the DRS results showed that the N/TiO2 powders had absorption in the visible light region under the wavelength of 550nm,the photodegradation on methylene orange showed the N/TiO2 powders calcined at 700℃ exhibited the best photocatalytic activity and the removal rate was up to 69.7% under 120min visible light irradiation.
参考文献
| [1] | 尹京花,赵莲花,武伦鹏,张海明.掺铁TiO2纳米微粒的制备及光催化活性[J].分子催化,2006(06):569-573. |
| [2] | 卢维奇,赵黎明,刘弋璐,黄肖容.镧或钕掺杂TiO2可见光催化剂及其对甲基橙的降解活性[J].稀土,2006(01):30-32. |
| [3] | 井立强,李晓倩,李姝丹,王百齐,辛柏福,付宏刚,王德军,蔡伟民.纳米Au/TiO2光催化剂的XPS和SPS研究[J].催化学报,2005(03):189-193. |
| [4] | Wang H;Lewis JP .Second-generation photocatalytic materials: anion-doped TiO2[J].Journal of Physics. Condensed Matter,2006(2):421-434. |
| [5] | Asahi R;Morikawa T;Ohwaki T et al.[J].Science,2001,293:269-271. |
| [6] | Yuan Jian;Chen Mingxia;Shi Jianwei et al.[J].International Journal of Hydrogen Energy,2006,31:1326-1331. |
| [7] | Kang I C et al.[J].Journal of Photochemistry and Photobiology A:Chem,2007,02:003. |
| [8] | Wang Yan;Feng Caixia;Jin Zhensheng et al.[J].Journal of Molecular Catalysis A:Chemical,2006,1-3 |
| [9] | Shah S I;Li W;Huans C P et al.[J].Pans,99(10):6482-6486. |
| [10] | Yamsshita H;Ichihashi;Zhang S G .[J].Applied Surface Science,1997,1211122:305-309. |
| [11] | Yu JC.;Yu JU.;Ho WK.;Jiang ZT.;Zhang LH. .Effects of F- doping on the photocatalytic activity and microstructures of nanocrystalline TiO2 powders[J].Chemistry of Materials,2002(9):3808-3816. |
| [12] | Kumar PM.;Sastry M.;Badrinarayanan S. .Nanocrystalline TiO2 studied by optical, FTIR and X-ray photoelectron spectroscopy: correlation to presence of surface states[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2000(1/2):122-130. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%