制备出一种缓释型的沥青路面用防冰材料，由氯化钙与丙烯酸酯类聚合物，经化学处理而复合而成。合成的丙烯酸酯类聚合物能均匀包覆在氯化钙表面，从而有效控制氯化钙的释放速度，延长防冰材料的使用寿命。应用该防冰材料铺筑的沥青路面能够在0~-10℃内不结冰，防冰材料可缓慢释放，使用年限可达到5~10年，但不影响沥青路面的路用性能。
In the thesis,a anti-freezing material for asphalt pavement was prepared by special chemical process-ing with calcium chloride and acrylate polymers. The rate of release of calcium chloride was effectively controlled by acrylate polymers which evenly encapsulated,so it can prolong the service life of anti-freezing material. The as-phalt pavement which used the release anti-freezing material could unfrozen in 0~10℃ for 5~10 years times,but not affected the performance of the road.
参考文献
| [1] | Eric C;Lohrey,P. E .Field Evaluation of an Ex-perimental Bituminous Pavement Utilizing an Ice-Retardant Additive-Verglimit. March 1992. Tech-nical Report:FHWA-CT-RD-92-41085-F-92-4[R]. |
| [2] | M. Stroup-Gardiner .Use of Verglimit Deicing Product on El Dorado County Highway 50 PM 38. 6 to 39. 7 March 23,2008,Technical Report:CP2-2008-103 TB[R]. |
| [3] | 赵可;孟勇军;陈仕周 等.一种多孔蓄盐集料及其制备方法[P].CN101786834 |
| [4] | 崔龙锡 .蓄盐类沥青混合料研究[D].重庆交通大学,2010. |
| [5] | 张丽娟 .盐化物融雪沥青混合料研究[D].长安大学,2010. |
| [6] | 孟勇军;陈仕周;赵可 等.一种沥青混凝土碎石封层用抗凝冰剂及其制备方法[P].CN101787216 |
| [7] | 岳金文 .硝酸铵表面改性工艺研究[D].湖南大学,2003. |
| [8] | 潘祖仁.高分子化学[M].北京:化学工业出版社:45. |
| [9] | 中原;竹田;島崎.凍結抑制効果の予測法に閞する検討[A].,1995:530-531. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%