The precipitation behavior of Co phases in B2-ordered (Ni, Co)Al has been investigatedin terms of transmission electron microscopy. Fine precipitation off cc-Co occurs in(Ni, Co)Al by aging at temperature over 973K. The orientation relationship betweenthe fcc-Co precipitates and the B2-(Ni, Co)Al matrix follows the Kurdjumow-Sachs(K-S) orientation relation. But when the aging temperature is under 873K the Coprecipitates have a hcp crystal structure. The orientation relationship between thehcp-Co precipitates and the B2-(Ni, Co)Al matrix follows the Burgers orientation re-lation. (Ni, Co)Al is hardened appreciably by the fine precipitation of both the fcc-Coand hcp-Co phases. The temperature dependence of the yield strength of precipitate-containing B2-ordered (Ni, Co)Al was investigated by compression tests over the rangeof 298-1273K. The fine precipitation of Co phases enhances greatly the low and in-termediate temperature yield strength. When the deformation temperature was over873K, the strength of precipitate-containing (Ni, Co)Al is comparable to ternary dual-phase (Ni, Co)Al+Ni3Al alloy.
参考文献
| [1] | M V Nathal.[A].NATO ASI Series E,Kluwer Academic Pub ,Dordrecht,1992:541. |
| [2] | R Darolia .[J].Journal of Metals,1991,43:44. |
| [3] | K Ishida;R Kainuma;N Ueno;T Nishizawa .[J].Metallurgical and Materials Transactions,1991,A22:441. |
| [4] | W H Tian;M Hibino;M Nemoto .[J].Intermetallics,1998,6(06):121. |
| [5] | P Hansen.Physikalische Metallkunde[M].Auflage,Springer,Berlin,1984:274. |
| [6] | S Nagasaki .[J].Metals,1992(62):121. |
| [7] | D L Wood;J H Westbrook .[J].Transactions of the Metallurgical Society of AIME,1962,224:1024. |
| [8] | A R Causey;E Teghtsoonian .[J].Metallurgical and Materials Transactions,1970,1(01):1177. |
| [9] | R T Pascoe;C W A Newey .[J].Metal Science Journal,1968,2(02):138. |
| [10] | Y Kimura;T Suzuki;Y Mishima.[A].MRS,Pittsburg,1993:697. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%