为了研究激光熔覆镍基合金涂层显微组织与性能之间的关系,本文选用Ni25、Ni45、Ni60镍基自熔性合金粉末作为熔覆材料,在同一工艺参数下在45(#)钢基体上制得Ni25、Ni45、Ni60合金激光熔覆涂层.利用扫描电子显微镜(SEM)、能谱仪(EDS)、X射线衍射仪(XRD)、显微硬度计等方法对涂层的显微组织、物相组成、显微硬度等进行了研究.结果表明从Ni25到Ni60合金涂层,随着合金元素含量的提高,涂层微观组织逐渐由亚共晶转变为过共晶,γ-Ni奥氏体枝晶所占体积分数减少,尺寸细化,枝晶间的共晶组织和硬质相所占的体积分数增大,涂层和基体之间结合带的宽度越来越窄,熔覆层的显微硬度越来越高.Ni25、Ni45合金涂层的平均显微硬度分别为250HV和550HV左右,而Ni60合金涂层的平均硬度却高达750HV左右,为Ni25合金涂层的3倍.
参考文献
| [1] | X.L. Wu;G.N. Chen .Microstructural features of an iron-based laser coating[J].Journal of Materials Science,1999(14):3355-3361. |
| [2] | Da-wei Zhang;T. C. Lei;Ji-ge Zhang;Jia-hu Ouyang .The effects of heat treatment on microstructure and erosion properties of laser surface-clad Ni-based alloy[J].Surface & Coatings Technology,1999(2/3):176-183. |
| [3] | 董世运,马运哲,徐滨士,韩文政.激光熔覆材料研究现状[J].材料导报,2006(06):5-9,13. |
| [4] | H. Chen;C. Xu;J. Qu;I. M. Hutchings;P. H. Shipway;J. Liu .Sliding wear behaviour of laser clad coatings based upon a nickel-based self-fluxing alloy co-deposited with conventional and nanostructured tungsten carbide-cobalt hardmetals[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2005(2):801-806. |
| [5] | 冯莉萍,林鑫,陈大融,李延民,杨海欧,黄卫东.材料对激光多层涂覆定向凝固显微组织的影响[J].航空材料学报,2004(01):7-11. |
| [6] | 冯旭东.激光熔覆与热喷涂镍基合金涂层的微观组织和性能[J].热处理技术与装备,2010(01):28-31. |
| [7] | 高阳,佟百运,梁勇,师昌绪.不锈钢基体NiCrBSi/NiCrBSi（SiC-Mo）合金层的激光熔敷[J].清华大学学报(自然科学版),2003(06):754-757. |
| [8] | 伍天华,李文戈.原位自生WC-Cr_3C_2复相陶瓷增强铁基表面复合材料[J].材料科学与工程学报,2009(06):924-927. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%