通过溶剂热反应合成了Fe3O4空心微球.采用X射线衍射仪(XRD)、透射电子显微镜(TEM)和扫描电子显微镜(SEM)对样品的结构和形貌进行了表征.结果表明,所制备的单分散Fe3O4空心微球为立方多晶结构,其直径约400 nm,是由约40 nm纳米颗粒组装而成.用振动样品磁强计(VSM)测量了Fe3O4空心微球的室温和变温磁性.室温磁滞回线表明不同反应时间所得产物均表现为良好的亚铁磁性,其饱和磁化强度Ms随反应时间的增加先升后降.由反应时间为12 h所得的Fe3O4空心微球在1000 Oe下的M-T曲线测得其居里温度为778 K,并测得其在外磁场H=5000 Oe场冷却至液氮温度再升至不同温度(100 K,200 K,300 K)时的磁滞回线,发现不同温度时测得的Fe3O4空心微球磁滞回线都是左右对称的,没有明显的交换偏置效应,且随测量温度增加,其饱和磁化强度Ms和矫顽力Hc均降低.
参考文献
| [1] | Kim S W;Kim M;Lee W Y et al.Fabrication of Hollow Palladium Spheres and Their Successful Application to the Recyclable Heterogeneous Catalyst for Suzuki Coupling Reactions[J].Journal of the American Chemical Society,2002,124:7642-7643. |
| [2] | Tan B;Rankin SE .Dual latex/surfactant templating of hollow spherical silica particles with ordered mesoporous shells[J].Langmuir: The ACS Journal of Surfaces and Colloids,2005(18):8180-8187. |
| [3] | Yin ding;Yong Hu;Xiqun Jiang .Polymer-Monomer Pairs as a Reaction System for the Synthesis of Magnetic Fe_3O_4-Polymer Hybrid Hollow Nanospheres[J].Angewandte Chemie,2004(46):6369-6372. |
| [4] | Zhu LP;Xiao HM;Zhang WD;Yang G;Fu SY .One-pot template-free synthesis of monodisperse and single-crystal magnetite hollow spheres by a simple solvothermal route[J].Crystal growth & design,2008(3):957-963. |
| [5] | Lou XW;Yuan CL;Rhoades E;Zhang Q;Archer LA .Encapsulation and Ostwald ripening of Au and Au-Cl complex nanostructures in silica shells[J].Advanced functional materials,2006(13):1679-1684. |
| [6] | Chen XY;Zhang ZJ;Li XX;Shi CW .Hollow magnetite spheres: Synthesis, characterization, and magnetic properties[J].Chemical Physics Letters,2006(1-3):294-298. |
| [7] | Jia BP;Gao L .Morphological transformation of Fe3O4 spherical aggregates from solid to hollow and their self-assembly under an external magnetic field[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2008(3):666-671. |
| [8] | Yu D B;Sun X Q;Zou J W et al.Oriented Assembly of Fc3O4 Nanoparticles into Monodisperse Hollow Single-Crystal Microspheres[J].Journal of Physical Chemistry B,2006,110:21667-21671. |
| [9] | Xin-Hao Li;Dong-Hui Zhang;Jie-Sheng Chen .Synthesis of Amphiphilic Superparamagnetic Ferrite/Block Copolymer Hollow Submicrospheres[J].Journal of the American Chemical Society,2006(26):8382-8383. |
| [10] | Peng Hu;Lingjie Yu;Ahui Zuo .Fabrication of Monodisperse Magnetite Hollow Spheres[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2009(3):900-906. |
| [11] | 闫共芹,官建国,王维.热解-还原法制备单分散Fe3O4亚微空心球[J].物理化学学报,2007(12):1958-1962. |
| [12] | 吕庆荣,方庆清,刘艳美,尹萍.纳米结构四氧化三铁空心微球的合成及磁性研究[J].人工晶体学报,2010(03):656-659. |
| [13] | Zhongbing Huang;Fangqiong Tang .Preparation,structure,and magnetic properties of mesoporous magnetite hollow spheres[J].Journal of Colloid and Interface Science,2005(2):432-436. |
| [14] | 俞凌杰,袁方利,王熙.软模板法制备Fe3O4空心结构微球[J].过程工程学报,2008(02):394-398. |
| [15] | 范雄.金属X射线学[M].北京:机械工业出版社,1996:103-122. |
| [16] | Sun Y;Xia Y .Shape-Controlled Synthesis of Gold and Silver Nanoparticles[J].Science,2002,298:2167-2170. |
| [17] | Yuliang Wang;Xuchuan Jiang;Younan Xia .A Solution-Phase, Precursor Route to Polycrystalline SnO2 Nanowires That Can Be Used for Gas Sensing under Ambient Conditions[J].Journal of the American Chemical Society,2003(52):16176-16177. |
| [18] | Hong Deng;Xiaolin Li;Qing Peng;Xun Wang;Jinping Chen;Yadong Li .Monodisperse Magnetic Single-Crystal Ferrite Microspheres[J].Angewandte Chemie,2005(18):2782-2785. |
| [19] | R.Y. Hong;T.T. Pan;H.Z. Li .Microwave synthesis of magnetic Fe_3O_4 nanoparticles used as a precursor of nanocomposites and ferrofluids[J].Journal of Magnetism and Magnetic Materials,2006(1):60-68. |
| [20] | 刘锦宏,张凌飞,田庚方,李济晨,李发伸.低温固相反应法制备的NiFe2O4纳米颗粒的结构与磁性[J].物理学报,2007(10):6050-6055. |
| [21] | 吕庆荣,方庆清,刘艳美.纳米结构CoxFe3-xO4多孔微球的磁性及交换偏置效应研究[J].物理学报,2011(04):656-662. |
| [22] | 张有纲.磁性材料[M].成都:成都电讯工程学院出版社,1988:22. |
| [23] | Gupta A;Gong G Q;Xiao G et al.Grain-Boundary Effects on the Magnetoresistance Properties of Perovskite Manganite Films[J].Physical Review B,1996,54:R15629-R15632. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%