为了实现汽车零部件环境友好型镀锌防腐蚀处理,利用纳米镀锌和电泳涂装技术的有机结合,分别对酸性和碱性镀液电镀锌进行纳米改性研究.采用金相显微镜和场发射扫描电子显微镜(FE-SEM)研究镀锌层的表面形貌以及复合镀层的断面形貌；测量了镀锌层的塔菲尔(Tafel)曲线；采用百格刀法测试层间结合力并对复合镀层进行中性盐雾试验.结果表明,两种镀锌层均出现纳米晶；随着镀锌电流密度的增大两种镀锌层的腐蚀电位均增大,同时腐蚀电流密度降低；复合镀层中性盐雾试验耐腐蚀时间达到1000 h且结合力达到5B水平,这表明纳米晶镀锌层和电泳漆层具有良好的结合力和耐腐蚀性能.
参考文献
| [1] | Veeraraghavan B.;Slavkov D.;Prabhu S.;Nicholson M.;Haran B.;Popov B. Heimann B. .Synthesis and characterization of a novel non-chrome electrolytic surface treatment process to protect zinc coatings[J].Surface & Coatings Technology,2003(1):41-51. |
| [2] | Mouanga M;Ricq L;Douglade J;Bercot P .Effects of some additives on the corrosion behaviour and preferred orientations of zinc obtained by continuous current deposition[J].Journal of Applied Electrochemistry,2007(2):283-289. |
| [3] | Muralidhara HB;Naik YA .Electrochemical deposition of nanocrystalline zinc on steel substrate from acid zincate bath[J].Surface & Coatings Technology,2008(14):3403-3412. |
| [4] | 陈锦虹,任艳萍,卢锦堂,许乔瑜,孔纲.镀锌层三价铬钝化的研究进展[J].材料保护,2004(11):32-34. |
| [5] | 于元春,李宁,胡会利,张景双,屠振密.无铬钝化与三价铬钝化的研究进展[J].表面技术,2005(05):6-9. |
| [6] | 张振国,汤峰.锌铁合金化钢板镀层结构及防腐蚀性能的研究[J].材料保护,2005(08):51-53. |
| [7] | 曹莹,沈天慧,姚锦元,丁桂甫.电沉积纳米锌层的研究[J].电化学,2004(01):107-111. |
| [8] | I.Krylova .Painting by electrodeposition on the eve of the 21st century[J].Progress in Organic Coatings: An International Review Journal,2001(3/4):119-131. |
| [9] | 齐智远,孙淑萍.阴极电泳涂装的应用及发展[J].电镀与精饰,2006(06):22-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%